Objective
Since the transmittance of ceramics can influence the degree of conversion (DC) of resin cements, ceramics composition and shade should be considered in the selection of resin cement. This
in vitro
study aimed to evaluate the effect of the transmittance of different composition, opacities and shades of ceramics on the degree of conversion of two dual-cured resin cements.
Methodology
Sixty discs were prepared from low translucency (LT) and medium opacity (MO) lithium disilicate ceramic, and zirconia ceramic (Z). Each group was subdivided into 5 subgroups (n=4) in shades A2, A3.5, B2, C2 and D3. The transmittance measurement was performed in a spectrophotometer. The Variolink II and Rely X U200 resin cements were photoactivated by LED (1400 mW/cm2) for 40 s through the ceramic discs and without the discs (control group). The DC was measured with infrared FTIR spectroscopy, immediately after light activation. Data were analyzed with Kruskall-Wallis and one-way ANOVA, following post-hoc comparisons by Tukey test and Pearson’s correlation test (P<0.05).
Results
LT ceramic exhibited higher transmittance values compared to MO and Z ceramics. LTA2 and LTB2 showed statistically higher transmittance values compared to MOA2, MOA3.5 and ZA3.5. For Variolink II, the ceramic interposition did not influence the DC, since there were no statistical differences between groups with ceramic interposition and the control group. For Rely X U200 cement, the interposition of some ceramics types/shades (LTA3.5, MOA2, MOA3.5 and ZA3.5) significantly decreased the DC values compared to control group. A positive correlation was found between the ceramic transmittance and DC values of both tested cements. Conclusions. The transmittance and DC values of the cements were influenced by composition and shades of the ceramics. The higher the transmittance of ceramics, the higher the DC values for both cements.
Purpose
To evaluate the
push-out
bond strength (PBS) and failure mode of single adjustable (SAP) and customized (CP) posts cemented to root canal dentin using conventional (RelyX Ultimate) or self-adhesive (RelyX U200) dual-cure resin cements.
Methods
Herein, 40 bovine mandibular incisors were divided into four groups (n = 10): SAP cemented with RelyX Ultimate (SAP-UT), SAP cemented with RelyX U200 (SAP-U2), CP cemented with RelyX Ultimate (CP-UT), and CP cemented with RelyX U200 (CP-U2). PBS and failure modes were analyzed. Three-way repeated measures ANOVA test followed by Tukey’s test and Fisher–Freeman–Halton exact test were used for data analysis (α = 5%).
Results
The PBS values for SAP (p < .05) were higher than those for CP and were not influenced by the root third and resin cement (p > .05). When conventional resin cement was used, the SAP showed significant differences compared to CP (p < .05). When cemented with RelyX Ultimate, a higher prevalence of mixed and adhesive failures for SAP and CP, respectively, was observed (p < .05). For the self-adhesive resin cement, the failures were mostly adhesive (p < .05).
Conclusion
SAP showed better performance than CP. The root third and resin cements did not influence the PBS. The most prevalent failures were adhesive and mixed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.