No abstract

No abstract

No abstract

Different aggregate gradations of asphalt concrete possess dissimilar skeleton structures, leading to diverse macroscopic and mechanical characteristics. Acoustic emission (AE) technology can realize real-time monitoring of the whole damage evolution process of materials. The objective of the present investigation was to demonstrate the fracture characteristics of asphalt concrete with three types of aggregate gradations, including dense-graded asphalt concrete (AC), stone mastic asphalt (SMA), and open-graded friction course (OGFC) under indirect tensile load on account of the acoustic emission (AE) technique. The Marshall compaction method was used to prepare specimens, and the indirect tensile test (IDT) and AE monitoring were conducted simultaneously at different temperatures. The corresponding AE parameters containing energy, cumulative energy, count, and cumulative count were adopted to characterize the fracture process of asphalt concrete with different aggregate gradations. The impact of temperature on the damage characteristics of asphalt concrete was also assessed. Test results indicated that the AE parameters could effectively classify the damage stages of asphalt concrete, and specimens with different aggregate gradations exhibited different AE characteristics during failure processes. The combination of AE parameters and cumulative AE parameters can accurately characterize the damage characteristics of asphalt concrete. SMA specimens possessed the best overall performance among these three types of asphalt concrete in terms of the variations in energy and cumulative energy at different temperatures. The findings obtained in this study can provide a practical AE-based evaluation approach for demonstrating the fracture mechanism of asphalt concrete with different aggregate gradations.

Freeze–thaw (F–T) cycling and aging effects are the main factors contributing to the deterioration of asphalt mixtures. The acoustic emission (AE) technique enables real-time detection regarding the evolution of internal damage in asphalt mixtures during the loading process. This study set out to investigate the effects of F–T cycling and aging on the damage characteristics of asphalt mixture under splitting loads. Firstly, the Marshall specimens were prepared and then exposed to various numbers of F–T cycles (one, three, five, and seven) and different durations of aging (short-term aging and long-term aging for 24, 72, 120 and 168 h), after which the specimens were loaded by means of indirect tensile (IDT) testing, and corresponding parameters were synchronously collected by the AE acquisition system during the fracture process. Finally, the energy, cumulative energy and peak frequency were selected to investigate the damage mechanisms of asphalt mixtures. The findings demonstrate that the AE parameters provided effective identification of the deterioration for all specimens in real-time, and that the F–T cycling and aging effects altered the damage characteristics of asphalt mixtures, causing early damage, exacerbating the formation of micro-cracks in the early stage, accelerating the expansion of macro-cracks and advancing the debonding between the asphalt and aggregates. The findings of this study provide further insight into the mechanism of F–T cycling and aging effects on the deterioration of asphalt mixture.