Abstract. Cellulose nanofibres, 20 nm in diameter and 300 nm long, were prepared by acid hydrolysis of flax yarns. Composite films containing 2.5 and 5.0 wt% flax cellulose (FC) fibres were prepared by solution casting of mixtures of poly(lactic acid) (PLA) solution and cellulose nanofibre suspension in chloroform. The resulting composite films and solution cast pure PLA film, with thickness of around 160 μm, showed good transparency. For composites with 2.5 and 5.0 wt% FC, the tensile strength increased by 25 and 59% and tensile modulus by 42 and 47%, respectively, compared to pure PLA film. The composite film with 2.5 wt% FC combined high strength and ductility with tensile strength of 24.3 MPa and 70% elongation at break. Flax cellulose appeared to facilitate nucleation and subsequent crystallisation of PLA more effectively in the amorphous composites than in the crystalline composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.