Tribological behavior of biomedical ultrafine-grained (UFGed) TiNbZrTaFe (TNZTF) composites fabricated by powder metallurgy was investigated under dry wear condition. Results show that compared with two kinds of conventional biomedical Ti-6Al-4V (TAV) and Ti-13Nb-13Zr (TNZ) alloys, the wear loss of the TNZTF samples is only 3.5% and 1% of that of the TAV and TNZ samples, respectively. Unusual tribological behavior is that the wear loss of the TNZTF samples decreases with the increase in sliding speed at the same load. This is attributed to the formation of a large amount of hard Nb 2 O 5 particles on the contact surface of the material during rubbing and more severe plastic deformation in the material layers adjacent to the contact surfaces. The wear mechanism of the three kinds of alloys was also investigated. The outstanding tribological property proves that the UFGed TNZTF alloys should be an excellent candidate material to be used for biomedical application in the future.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.