Multi-walled carbon nanotubes (MWNTs) were incorporated into a linear low-density polyethylene (LLDPE) matrix through using screw extrusion and injection technique. The effect of different weight percent loadings of MWNTs on the morphology, mechanical, and thermal of LLDPE/MWNTs nanocomposite had been investigated. It was found that, at low concentration of MWNTs, it could uniformly disperse into a linear low-density polyethylene matrix and provide LLDPE/MWNTs nanocomposites much improved mechanical properties. Thermal analysis showed that a clear improvement of thermal stability for LLDPE/MWNTs nanocomposites increased with increasing MWNTs content.
A biomass based hydrogel soybean dregs-Poly(acrylic acid) (SD-PAA) was synthesized under UV radiation while using agricultural waste soybean dregs. Maximum absorption of SD-PAA is 3587 g·g−1 in distilled water and 302.0 g·g−1 in 150 mM NaCl aqueous solution. Moreover, the influence of granularity, salt solution, and ions in the solutions on water absorption is systematically studied. Sensitivity sequence of the hydrogel to cations was K+ < Na+ < NH4+ < Al3+ < Fe3+ < Mg2+ < Ca2+, and that to anions was PO43− > SO42− > Cl−. Moreover, the experimental results showed that SD-PAA water retention capability remained 37% after centrifugating for 60 min and 0.2% being dried at 60 °C for 70 h. Meanwhile, the swelling data agree well with the pseudo-second-order kinetic model and Fickian diffusion mechanism.
Fiber-reinforced polymer (FRP) materials are increasingly used in automotive industrial fields to achieve lightweight. In order to study the influence of high temperature and high humidity on the bonding structure between different materials, this paper selects basalt fiber-reinforced resin composite materials (BFRP) and aluminum alloy (Al), and uses Araldite® 2012 and Araldite® 2014, two adhesives, to make single lap joints (SLJs). The aging test was carried out for 0 (unaged), 10, 20, and 30 days under the environment of 80 °C/95% relative humidity (RH) and 80 °C/pure water. In this work, simple Fickian law was used to simulate the hygroscopic change law of dumbbell specimens of two adhesives and BFRP in a pure water environment. It was discovered that Araldite® 2012 is most affected by moisture, but the time to reach the maximum water absorption in Araldite® 2014 was shorter than in Araldite® 2012. The failure strength of the joint was obtained through a quasi-static tensile experiment, and it was found that the Araldite® 2014 adhesive joint first increased and then decreased in a high temperature environment. The strength increased by 11.63% after 20 days of aging under an 80 °C/95%RH environment, and increased by 16.66% after 10 days of aging under an 80 °C/pure water environment, which indicates that post-curing reaction occurred. The strength of Araldite® 2012 joints showed a downward trend. After 30 days of aging, it reduced by 40.38% under an 80 °C/95%RH environment and 41.11% under an 80 °C/pure water environment. By observing the load-displacement curve, it was found that, as time increased, the slope of the curve decreased, indicating that the stiffness of the bonded joint decreased with time. The failure modes of the joints were analyzed by macroscopic images and microscopic SEM methods, and the results showed that the surface failure transitions from a mixed failure to a complete tear failure over time. The failure of the basalt fiber/resin interface was because the interaction between the epoxy resin in the adhesive and the epoxy resin in BFRP was greater than the force between the basalt fiber layer and the epoxy resin layer in the BFRP sheet.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.