The external and internal connections have different mechanical, biological, and esthetical characteristics. Besides all systems that show proper success rates and effectiveness, crestal bone level maintenance is more important around internal connections than external connections. The Morse taper connection seems to be more efficient concerning biological aspects, allowing lower bacterial leakage and bone loss in single implants, including aesthetic regions. Additionally, this connection type can be successfully indicated for fixed partial prostheses and overdenture planning, since it exhibits high mechanical stability.
The material used for interim prostheses fabrication must present excellent physical properties for greater longevity in the face of environmental conditions, which can occur in the oral cavity. The purpose of this study was to evaluate the effect of a photopolymerized glaze on the physical and mechanical properties of polymers used for the fabrication of interim prostheses, before and after thermocycling and immersion in staining solutions. One hundred samples of composite and acrylic resins were fabricated: Dencor chemically activated acrylic resin (CAAR) (n=20) and heat-polymerized acrylic resin (HPAR) (n=20), Charisma (n=20), Structur (n=20), and Protemp (n=20). A mechanical polishing was performed on half of the samples, and a chemical polishing was performed on the remaining samples. Subsequently, all samples were submitted to thermocycling and immersion in coffee staining solution for 21days. Analysis of color and microhardness, as well as atomic force microscopy (AFM), scanning electron microscopy (SEM), and energy dispersive x-ray spectrometry (EDS) were performed. The data were submitted to repeated-measures analysis of variance (ANOVA), followed by the Tukey test (α=0.05) and the Student t-test (α=0.05). It was verified that the glaze decreased the chromatic alteration values, and increased the microhardness values of the samples, with the exception of the Charisma resin. The samples that did not receive chemical polishing had the greatest number of surface irregularities. This study concluded that the groups with glaze presented less color alteration. In addition, Charisma and Structur resins exhibited the greatest chromatic stability. As to the microhardness, the values were greater when the samples were treated with the glaze, with the exception of the Charisma group.
The effect of a photopolymerized glaze on different properties of acrylic resin (AR) for ocular prostheses submitted to accelerated aging was investigated. Forty discs were divided into 4 groups: N1 AR without glaze (G1); colorless AR without glaze (G2); N1 AR with glaze (G3); and colorless AR with glaze (G4). All samples were polished with sandpaper (240, 600 and 800-grit). In G1 and G2, a 1200-grit sandpaper was also used. In G3 and G4, samples were coated with MegaSeal glaze. Property analysis of color stability, microhardness, roughness, and surface energy, and assays of atomic force microscopy, scanning electron microscopy, and energy-dispersive spectroscopy were performed before and after the accelerated aging (1008h). Data were submitted to the ANOVA and Tukey Test (p<0.05). Groups with glaze exhibited statistically higher color change and roughness after aging. The surface microhardness significantly decreased in groups with glaze and increased in groups without glaze. The surface energy increased after the aging, independent of the polishing procedure. All groups showed an increase of surface irregularities. Photopolymerized glaze is an inadequate surface treatment for AR for ocular prostheses and it affected the color stability, roughness, and microhardness. The accelerated aging interfered negatively with the properties of resins.
Microwave-processed resin showed a significant reduction in cell proliferation and an increase in IL6 quantity. Heat-polymerized resin exhibited a higher mRNA expression of COL IV, MMP9, and TGFβ; this result was similar to that in the nonstimulated group.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.