AlN thin films were grown in a N2 atmosphere onto a Si/Si3N4 substrate by pulsed laser ablation. We have varied the substrate temperature for the thin film growth, using X-ray Reflectometry (XRR) analysis, we have characterized the thickness and density of the thin layer and the interface roughness from the X-ray reflectivity profiles. Experimental data showed that the root-mean-square roughness was in the range of 0.3 nm. X-ray photoelectron spectroscopy (XPS) was employed to characterize the chemical composition of the films. These measurements detected carbon and oxygen contamination at the surface. In the highresolution X-ray photoelectron spectroscopy Al2p data, binding energies for Al-N and Al-O species were identified but no Al-Al species were present. In the N1s data, N-O species were not detected, but chemically bonded O was present in the films as Al-O species. Furthermore the value of optical energy gap, Eg was about 5.3 (± 0.1) eV. The composition varied with process conditions, and the nitrogen content decreased in AlN films processed above 500°C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.