The objective of this study was to evaluate the influence of hydrofluoric acid (HF) and conditioning time on the micro-shear bond strength (µSBS) between dual-cure resin cement and glass-ceramic materials, such as lithium disilicate ceramic (IPS e.max CAD, Ivoclar Vivadent) (EX) and leucite-reinforced ceramic (IPS Empress CAD, Ivoclar Vivadent) (EP), and also a hybrid ceramic (Vita Enamic, Vita Zahnfabrik) (VE). Eighteen sections with 1 mm thickness were cut from each CAD/CAM material and randomly divided into three groups, according to the surface etching time (30 s, 60 s, 90 s). The surface treatment was performed using 9.5% HF acid gel, then resin cement was applied on the prepared ceramic plates and light cured. µSBS values between resin cement and the ceramic material were measured with a universal testing machine at a crosshead speed of 0.5 mm/min until the failure occurred. The fractured surfaces of specimens were microscopically evaluated, and failure modes were classified as: adhesive between resin cement and ceramic, cohesive within ceramic or cement and mixed failure. Surface roughness of etched samples was examined using a scanning electron microscope. Obtained data were statistically analysed using one-way analysis of variance (ANOVA) and Bonferroni post hoc test with a level of significance α = 0.05. The results of the statistical methods applied indicate that µSBS mean difference for leucite-reinforced ceramic (EP) was statistically significant (p < 0.05). However, µSBS values for hybrid ceramic (VE) and lithium disilicate ceramic (EX) were not affected, from a statistical point of view, by the conditioning time (p > 0.05).
In the present study are depicted valuable observations for practitioners, obtained from an in vitro study which aims to evaluate the compressive strength of occlusal veneers fabricated from 3 type of restorative materials, before and after 1 month of acidic artificial saliva exposure (pH = 2.939). In this context, 90 extracted human molars were prepared to receive computer-aided design/computer-aided manufacturing (CAD/CAM) occlusal veneers. The restorative materials considered in this study were: Cerasmart; Straumann Nice and Tetric CAD. The occlusal veneers were designed, milled and cemented with an adhesive dual-cure resin cement. From all the extracted human molars, only sixty specimens were immersed in acidic artificial saliva, for 1 month, at 37 °C ± 1 °C and part of this specimens were also thermo-cycled, between 5 and 55 °C ± 2 °C, before compressive strength test. The results showed a lower compressive strength for both the samples exposed to acidic artificial saliva as well as for the samples exposed to acidic artificial saliva and thermo-cycled. Scanning electron microscopy (SEM) showed that after compressive strength, all the specimens non-exposed to acidic artificial saliva, present extensive cracks formation at the surface of the restorations, and after exposure to acidic artificial saliva for 1 month, the surface damage was characterized by longitudinal and profound fractures of the restoration, as well as the fracture of the tooth structure. Between CAD/CAM materials tested, nanoceramic resin shows more favorable fracture patterns, both before and after acidic artificial saliva exposure.
Polymer infiltrated ceramics are hybrid materials that combine the strength of ceramics and the flexibility of polymers. The aim of this study was to compare the fracture load capacity of monolithic CAD/CAM crowns with different occlusal thicknesses, made from polymer infiltrated ceramic network. Fifteen full contour CAD/CAM crowns made of Vita Enamic with occlusal thicknesses of 0.5 mm, 1.0 mm and 1.5 mm were fabricated with a wet milling machine. Restorations were cemented on human molars with adhesive cement. Samples were loaded along the long axis until fracture, with a single static compressive force. A scanning electron microscope (SEM) was used to examine the fracture surface of specimens after the fracture. The results of this study reveals that the fracture load of the samples increased progressively with the occlusal thickness. The highest fracture value was recorded for1.5 mm occlusal thickness of the crown. No statistically significant difference was reported between the three experimental groups. It can be concluded that hybrid monolithic CAD-CAM crowns showed sufficient fracture strength to be used for single restorations in the posterior area, even with a reduced occlusal thickness.
In the original publication of the article, the author "Daniel Pop" was published as co-corresponding author and cocorresponding authorship is removed from "Daniel Pop" in this article. The original article has been updated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.