Polypropylene (PP) has become the most promising and candidate material for fabricating lightweight products. Microcellular injection molding (MIM) is a cost-effective technology for manufacturing porous plastic products. However, it is still challenging to fabricate high-performance PP microcellular components. Herein, we reported an efficient strategy to produce lightweight and high impact toughness foamed PP/polyethylene terephthalate (PET)/polyolefin-based elastomer (POE) components by combining in situ fibrillation (INF) and MIM technologies. First, the INF composite was prepared by integrating twin-screw compounding with melt spinning. SEM analysis showed PET nanofibrils with a diameter of 258 nm were achieved and distributed uniformly in the PP due to the POE’s inducing elaboration effect. Rheological and DSC analysis demonstrated PET nanofibrils pronouncedly improved PP’s viscoelasticity and crystal nucleation rate, respectively. Compared with PP foam, INF composite foam showed more stretched cells in the skin layer and refined spherical cells in the core layer. Due to the synergistic toughening effect of PET nanofibrils and POE elastic particles, the impact strength of INF composite foams was 295.3% higher than that of PP foam and 191.2% higher than that of melt-blended PP/PET foam. The results gathered in this study reveal potential applications for PP based INF composite foams in the manufacturing of lightweight automotive products with enhanced impact properties.

With the increasing demand for plastic components, the development of lightweight, high strength and functionalized polypropylene (PP) from a cost-effective and environmentally friendly process is critical for resource conservation. In situ fibrillation (INF) and supercritical CO2 (scCO2) foaming technology were combined in this work to fabricate PP foams. Polyethylene terephthalate (PET) and poly(diaryloxyphosphazene)(PDPP) particles were applied to fabricate in situ fibrillated PP/PET/PDPP composite foams with enhanced mechanical properties and favorable flame-retardant performance. The existence of PET nanofibrils with a diameter of 270 nm were uniformly dispersed in PP matrix and served multiple roles by tuning melt viscoelasticity for improving microcellular foaming behavior, enhancing crystallization of PP matrix and contributing to improving the uniformity of PDPP’s dispersion in INF composite. Compared to pure PP foam, PP/PET(F)/PDPP foam exhibited refined cellular structures, thus the cell size of PP/PET(F)/PDPP foam was decreased from 69 to 23 μm, and the cell density increased from 5.4 × 106 to 1.8 × 108 cells/cm3. Furthermore, PP/PET(F)/PDPP foam showed remarkable mechanical properties, including a 975% increase in compressive stress, which was attributed to the physical entangled PET nanofibrils and refined cellular structure. Moreover, the presence of PET nanofibrils also improved the intrinsic flame-retardant nature of PDPP. The synergistical effect of the PET nanofibrillar network and low loading of PDPP additives inhibited the combustion process. These gathered advantages of PP/PET(F)/PDPP foam make it promising for lightweight, strong, and fire-retardant polymeric foams.