Recently researches on starch nanocrystals (SNC) production have become of interest due to their many applications, especially as reinforcement in polymeric matrices. Quinoa starch (QS) has desirable characteristics for SNC production such as small granule size and relatively low amylose content. Thus, the objective of this research was to produce quinoa SNC (QSNC) by acid hydrolysis at different temperatures (30, 35 and 40) °C. Furthermore, the effect of QSNC addition on the structural and physical properties of cassava starch films was studied. QS presented different percentages of hydrolysis on the fifth day, 63%, 73% and 91% for (30, 35 and 40) °C, respectively. QS (0.59 days-1) was hydrolyzed more rapidly than waxy maize starch (0.39 days-1) at 40 °C. QSNC yields decreased with temperature increase from (30 to 40) °C, while the relative crystallinity was not altered (~35%). The morphology of QSNC produced at 30 °C was irregular with micrometric size while those produced at 35 °C and 40 °C presented parallelepiped shapes with sizes between 50 nm and 100 nm and 400 nm to 900 nm (aggregates). The hydrodynamic diameter and the thermal properties of QSNC decreased with temperature increase, while the FTIR band intensities and the zeta potential increased. The properties indicated that quinoa QSNC were only obtained at (35 and 40) °C with yields of 22.8% and 6.8%, respectively. QSNC produced at 40 °C presented lower yield and crystallinity than waxy maize SNC, but a lower hydrodynamic diameter. Thus, based on the yield and transition temperature, QSNC produced at 35 °C was selected for application in cassava starch films. The films were prepared by casting technique, with 4 g of cassava starch / 100 g of film forming dispersion; 25 g glycerol / 100 g starch; and 0; 2.5; 5.0 and 7.5 g of QSNC / 100 g of starch. X-ray diffractograms confirmed the presence of QSNC in the films. Addition of QSNC to films increased the roughness and the contact angle at 5.0% and 7.5% concentrations, the tensile strength and elastic modulus, the color parameters L* and a* at 7.5% concentration, and the opacity; while decreasing deformation at break, water vapor permeability at 5.0% concentration, and gloss. Other film properties such as thickness, moisture content, solubility, thermal properties were not affected by QSNC addition. The results indicated that the QSNC produced at 35 ° C can be used as reinforcement in nanocomposite films to improve their mechanical properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.