Fire is one of the most unfavorable conditions that cement-based composites can face during their service lives. The uniaxial tensile and flexural tensile properties of the steel-polyvinyl alcohol fiber-calcium carbonate whisker (CW) multi-scale fiber reinforced cement matrix composites (MSFRCs) under high temperatures are studied, including strength, deformation capacity, energy dissipation capacity, and its ability to be assessed through the empirical calculation method. The study showed that with the increase of the treatment temperature, the MSFRC residual bending strength, bending toughness, and tensile strength decreased overall, but the decline was slow at 600 °C. The peak flexural deflection and peak tensile strain of MSFRC first reduced and then increased with the increase of the temperature. As the temperature increased, the nominal stiffness of MSFRC bending and straight gradually reduced, and the rate of decline was faster than that of its strength. However, the uniaxial tensile properties were more sensitive to the temperature and degraded more rapidly. A quantitative relationship was established between MSFRC residual bending, tensile strength, and temperature. A comparison with existing research results shows that MSFRC has achieved an ideal effect of high temperature resistance. The multi-scale hybrid fiber system significantly alleviates the deterioration of cement-based composite’s mechanical properties under high temperatures. With the help of an optical microscope and scanning electron microscope (SEM), the high temperature influence mechanism on the uniaxial tensile and flexural properties of MSFRC was revealed.

Currently, low heat Portland (LHP) cement is widely used in mass concrete structures. The magnesia expansion agent (MgO) can be adopted to reduce the shrinkage of conventional Portland cement-based materials, but very few studies can be found that investigate the influence of MgO on the properties of LHP cement-based materials. In this study, the influences of two types of MgO on the hydration, as well as the shrinkage behavior of LHP cement-based materials, were studied via pore structural and fractal analysis. The results indicate: (1) The addition of reactive MgO (with a reactivity of 50 s and shortened as M50 thereafter) not only extends the induction stage of LHP cement by about 1–2 h, but also slightly increases the hydration heat. In contrast, the addition of weak reactive MgO (with a reactivity of 300 s and shortened as M300 thereafter) could not prolong the induction stage of LHP cement. (2) The addition of 4 wt.%–8 wt.% MgO (by weight of binder) lowers the mechanical property of LHP concrete. Higher dosages of MgO and stronger reactivity lead to a larger reduction in mechanical properties at all of the hydration times studied. M300 favors the strength improvement of LHP concrete at later ages. (3) M50 effectively compensates the shrinkage of LHP concrete at a much earlier time than M300, whereas M300 compensates the long-term shrinkage more effectively than M50. Thus, M300 with an optimal dosage of 8 wt.% is suggested to be applied in mass LHP concrete structures. (4) The addition of M50 obviously refines the pore structures of LHP concrete at 7 days, whereas M300 starts to refine the pore structure at around 60 days. At 360 days, the concretes containing M300 exhibits much finer pore structures than those containing M50. (5) Fractal dimension is closely correlated with the pore structure of LHP concrete. Both pore structure and fractal dimension exhibit weak (or no) correlations with shrinkage of LHP concrete.

Fiber is effective in restricting cracks and improving the toughness of geopolymer composites, but few studies have focused on the surface crack characteristics of fiber-reinforced geopolymer composites. In this paper, after flexural tests of polypropylene fiber-reinforced geopolymer mortar, the surface cracking image was collected by a digital camera and cracking information was extract by deep learning. Finally, the cracking and fractal characteristics were specifically discussed. The semantic segmentation network can accurately extract surface cracks for calculating various parameters. The results showed that the mean intersection over union (mIoU) and mean pixel accuracy (mPA) of the cracks are 0.8451 and 0.9213, respectively. Generally, the crack length, width, area, and fractal dimension of the specimen are all increased with the increase in the fiber volume fraction. These crack parameters grow rapidly when the fiber content is small, and the growth of the crack parameters gradually slows down as the fiber volume fraction increases to approximately 1.5%. The highest crack parameter values were found in the geopolymer mortar, with a 0.48 water–binder ratio and 12 mm fiber length. The variation of the bottom crack length and the side crack fractal dimension can be used to represent the overall crack variation patterns. Meanwhile, the crack parameters increase with the increased fiber factor in a quadratic function. Based on these crack parameters, the critical fiber factor and dense fiber factor of polypropylene fiber-reinforced geopolymer mortar were 200 and 550, respectively. They are greater than those of fiber-reinforced Portland cementitious composites. The influence of various crack parameters on the flexural strength is in the order of the crack area, width, length, and fractal dimension.