CaF 2 nanoparticles doped with 1 at. % Eu 3+ and codoped with Mn 2+ ions (1, 2, and 3 at. %) were synthesized at 180 °C by using ethylene glycol as a capping agent and solvent medium. The emission spectra of these nanomaterials show two main peaks at 590 and 612 nm after excitation at 240 or 394 nm. Enhancement in luminescence is found upon codoping of Mn 2+ . Parts of Eu 3+ ions are substituted into Ca 2+ sites (having a symmetry environment), which is reflected in the higher probability of magnetic dipole transition over that of electric dipole transition. The polymer film of polyvinyl alcohol incorporated with CaF 2 :1Eu shows the red emission. The prepared nanomaterials are highly water dispersible. The hybrid of CaF 2 :1Eu and Fe 3 O 4 shows the heating ability up to 42 °C under an AC magnetic field. This is suitable for cancer therapy through hyperthermia. A very high specific absorption rate (SAR) of 283 W/g is observed. This can be ascribed to the increased magnetocrystalline anisotropy and Brownian relaxation. Biocompatibility of hybrid nanoparticles up to 75% in HeLa cells is observed. Also, this hybrid shows the red emission, and thus, it will be useful in tracing of magnetic nanoparticles through in vivo and in vitro optical imaging applications. Interestingly, the new exciton band at 300 nm is found in such a hybrid material.
SnO2:5Tb (SnO2 doped with 5 at% Tb(3+)) nanoparticles were synthesised by a polyol method and their luminescence properties at different annealing temperatures were studied. Characterization of nanomaterials was done by X-ray diffraction (XRD), Fourier transformation infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and vibrating sample magnetometry (VSM). XRD studies indicate that the prepared nanoparticles were of tetragonal structures. Upon Tb(3+) ion incorporation into SnO2, Sn(4+) changes to Sn(2+) and, on annealing again at higher temperature, Sn(2+) changes to Sn(4+). The prepared nanoparticles were spherical in shape. Sn-O vibrations were found from the FTIR studies. In photoluminescence studies, the intensity of the emission peaks of Tb(3+) ions increases with the increase of annealing temperature, and emission spectra lie in the region of white emission in the CIE diagram. CCT calculations show that the SnO2:5Tb emission lies in cold white emission. Quantum yields up to 38% can be obtained for 900 °C annealed samples. SnO2:5Tb nanoparticles were well incorporated into the PVA polymer and such a material incorporated into the polymer can be used for display devices. The SnO2:5Tb/Fe3O4 nanohybrid was prepared and investigated for hyperthermia applications at different concentrations of the nanohybrid. This achieves a hyperthermia temperature (42 °C) under an AC magnetic field. The hybrid nanomaterial SnO2:5Tb/Fe3O4 was found to exhibit biocompatibility with HeLa cells (human cervical cancer cells) at concentrations up to 74% for 100 μg L(-1). Also, this nanohybrid shows green emission and thus it will be helpful in tracing magnetic nanoparticles through optical imaging in vivo and in vitro application.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.