The mechanical performance of concrete with varying proportions of steel scraps as a composite additive is investigated in this work. A M50 grade concrete admixture with a 0.35 water-to-binder ratio was prepared for this study. The appropriate quantity of superplasticizer was included as the mineral admixture. Steel scraps are obtained as waste from local machining workshops and then included in various proportions, including 0.25, 0.5, 1.0, and 2.0 percentages. The cubical mortar specimens were being employed to determine the compressive characteristics of mortar structure with and without steel scrap, whilst the cylinder-formed specimens and beam shaped samples were being utilized to determine the indirect tensile strength and flexural strength of concrete mixture. All experiments with different percentages of steel scrap were conducted on the 3 replicates, and the mean value is provided in this paper. After 28 days, the cement without steel scrap seemed to have a mean compression, flexural, and tensile strengths of 46.3 MPa, 5.52 MPa, and 4.23 MPa, respectively, which were improved to 51.7 MPa, 6.16 MPa, and 4.58 MPa with the inclusion of 1.0% steel scrap. The proposed investigation will contribute to reducing cement use, hence reducing cement industry's adverse ecological impacts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.