Al2O3-coated Li(Ni0.6Co0.2Mn0.2)O2 cathode materials were prepared by simple surface modification in water media through a sol-gel process with a dispersant. The crystallinity and surface morphology of the samples were characterized through X-ray diffraction analysis and scanning electron microscopy observation. The Li(Ni0.6Co0.2Mn0.2)O2 cathode material was of a polycrystalline hexagonal structure and agglomerated with particles of approximately 0.3 to 0.8 μm in diameter. The nanosized Al2O3 particles of low concentration (0.06–0.12 wt %) were uniformly coated on the surface of Li(Ni0.6Co0.2Mn0.2)O2. Measurement of electrochemical properties showed that Li(Ni0.6Co0.2Mn0.2)O2 coated with Al2O3 of 0.08 wt % had a high initial discharge capacity of 206.9 mAh/g at a rate of 0.05 C over 3.0–4.5 V and high capacity retention of 94.5% at 0.5 C after 30 cycles (cf. uncoated sample: 206.1 mAh/g and 90.8%, respectively). The rate capability of this material was also improved, i.e., it showed a high discharge capacity of 166.3 mAh/g after 5 cycles at a rate of 2 C, whereas the uncoated sample showed 155.8 mAh/g under the same experimental conditions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.