Sub-microfibers and nanofibers have a high surface-to-volume ratio, which makes them suitable for diverse applications including environmental remediation and filtration, energy production and storage, electronic and optical sensors, tissue engineering, and drug delivery. However, the use of such materials is limited by the low throughput of established manufacturing technologies. This short report provides an overview of current production methods for sub-microfibers and nanofibers and then introduces a new melt-electrospinning prototype based on a spinneret with 600 nozzles, thereby providing an important step towards larger-scale production. The prototype features an innovative collector that achieves the optimal spreading of the fiber due to its uneven surface, as well as a polymer inlet that ensures even polymer distribution to all nozzles. We prepared a first generation of biobased fibers with diameters ranging from 1.000 to 7.000 μm using polylactic acid and 6% ( w /w) sodium stearate, but finer fibers could be produced in the future by optimizing the prototype and the composition of the raw materials. Melt electrospinning using the new prototype is a promising method for the production of high-quality sub-microfibers and nanofibers.

Sub-microfibers and nanofibers produce more breathable fabrics than coarse fibers and are therefore widely used in the textiles industry. They are prepared by electrospinning using a polymer solution or melt. Solution electrospinning produces finer fibers but requires toxic solvents. Melt electrospinning is more environmentally friendly, but is also technically challenging due to the low electrical conductivity and high viscosity of the polymer melt. Here we describe the use of colorants as additives to improve the electrical conductivity of polylactic acid (PLA). The addition of colorants increased the viscosity of the melt by >100%, but reduced the electrical resistance by >80% compared to pure PLA (5 GΩ). The lowest electrical resistance of 50 MΩ was achieved using a composite containing 3% (w/w) indigo. However, the thinnest fibers (52.5 µm, 53% thinner than pure PLA fibers) were obtained by adding 1% (w/w) alizarin. Scanning electron microscopy revealed that fibers containing indigo featured polymer aggregates that inhibited electrical conductivity, and thus increased the fiber diameter. With further improvements to avoid aggregation, the proposed melt electrospinning process could complement or even replace industrial solution electrospinning and dyeing.

Electrospinning is widely used for the manufacture of fibers in the low-micrometer to nanometer range, allowing the fabrication of flexible materials with a high surface area. A distinction is made between solution and melt electrospinning. The former produces thinner fibers but requires hazardous solvents; whereas the latter is more environmentally sustainable because solvents are not required. However, the viscous melt requires high process temperatures and its low conductivity leads to thicker fibers. Here, we describe the first use of the biobased dyes alizarin; hematoxylin and quercetin as conductive additives to reduce the diameter of polylactic acid (PLA) fibers produced by melt electrospinning; combined with a biobased plasticizer to reduce the melt viscosity. The formation of a Taylor cone followed by continuous fiber deposition was observed for all PLA compounds; reducing the fiber diameter by up to 77% compared to pure PLA. The smallest average fiber diameter of 16.04 µm was achieved by adding 2% (w/w) hematoxylin. Comparative analysis revealed that the melt-electrospun fibers had a low degree of crystallinity compared to drawn filament controls—resembling partially oriented filaments. Our results form the basis of an economical and environmentally friendly process that could ultimately, provide an alternative to industrial solution electrospinning

Sub-microfibers are polymer filaments less than 1 µm in diameter that can be fabricated into highly flexible materials with a large specific surface area. They are often produced by solvent or melt electrospinning. The former is a scalable process that produces thinner fibers but requires hazardous solvents, whereas the latter is more environmentally sustainable due to the absence of solvents but is more challenging to scale up. Here we investigated the manufacturing of biobased polylactic acid (PLA) sub-microfibers by melt electrospinning using a single-nozzle laboratory-scale device and a novel 600-nozzle pilot-scale device combined with conductive and viscosity-reducing additives: sodium stearate (NaSt), sodium chloride (NaCl) and a polyester-based plasticizer. We determined the effect of different additive concentrations on fiber diameter, thermal properties, polymer degradation, and fiber deposition. At the laboratory scale, the minimum average fiber diameter (16.44 µm) was accomplished by adding 2% (w/w) NaCl, but a stable spinning process was not achieved and the plasticizer did not reduce the melt viscosity. NaSt was the most effective additive in terms of adapting the material properties of PLA for melt electrospinning, but extensive polymer degradation occurred at higher temperatures and with higher concentrations of the additive. At the pilot-scale, the minimum average fiber diameter (3.77 µm) was achieved by adding 6% (w/w) NaSt, with a spinneret temperature of 195℃ and a spin pump speed of 0.5 rpm (0.16 cm3), without further improvements such as the integration of a heating chamber. The smallest single-fiber diameter (1.23 µm) was achieved under the same conditions but using a spin pump speed of 2 rpm. The scaled-up melt-electrospinning device therefore offers significant potential for the production of biobased sub-microfibers, bridging the gap between laboratory-scale and pilot-scale manufacturing.

AbstractMelt electrospinning has been used to manufacture fibers with diameters in the low micrometer range, but the production of submicrometer fibers has proven more challenging. In this study, we investigated the feasibility of fabricating polylactic acid nanofibers using polymer grades with the increasing melt flow rates (15–85 g/10 min at 210°C) by melt electrospinning with a 600-nozzle pilot-scale device featuring an integrated climate control system realized as a glass chamber around the spinneret. Previous experiments using this device without appropriate climate control produced fibers exceeding 1 µm in diameter because the drawing of fibers was inhibited by the rapid cooling of the polymer melt. The integrated glass chamber created a temperature gradient exceeding the glass transition temperature of the polymer, which enhanced the drawing of fibers below the spinneret. An average fiber diameter of 810 nm was achieved using Ingeo Biopolymer 6252, and the finest individual fiber (420 nm in diameter) was produced at a spin pump speed of 5 rpm and a spinneret set temperature of 230°C. We have therefore demonstrated the innovative performance of our pilot-scale melt-electrospinning device, which bridges the gap between laboratory-scale and pilot-scale manufacturing and achieves fiber diameters comparable to those produced by conventional solution electrospinning.