We report on the fabrication of high-performance ultra-thin-body (UTB) SnO2 thin-film transistors (TFTs) using microwave-irradiation post-deposition annealing (PDA) at a low process temperature (<100 °C). We confirm that the electrical characteristics of SnO2 TFTs become drastically enhanced below a body thickness of 10 nm. The microwave-annealed UTB SnO2 TFTs with a thickness of 5 nm exhibited increased optical transmittance, as well as remarkable transfer characteristics: a high mobility of 35.4 cm2 V−1 s−1, a drain current on/off ratio of 4.5 × 107, a steep subthreshold gate voltage swing of 623 mV/dec, and a clear enhancement-mode behavior. Additionally, the microwave-annealed SnO2 TFTs exhibited a better positive gate-bias stress/negative gate-bias stress immunity than thermally annealed SnO2 TFTs. Therefore, the thickness of the UTB SnO2 TFTs, as well as the microwave-annealing process, are both shown to be essential for transparent and flexible display technology.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.