No abstract

Implant failure has been attributed to loosening of an implant from the host bone possibly due to poor osseointegration. One promising strategy for improving osseointegration is to develop a functional implant surface that promotes osteoblast differentiation. In this study, a titanium (Ti) surface was functionalized by an anodic oxidation process and was loaded with recombinant human bone morphogenetic protein-2 (rhBMP-2). The following four groups of Ti surfaces were prepared: machined (M), anodized machined (MA), resorbable blast medium (RBM), and anodized RBM (RBMA). The surfaces were characterized by scanning electron microscopy and contact angle measurements. The results showed that a Ti oxide layer (TiO(2)) was observed in the anodized surfaces in the form of nanotubes, approximately 100 nm in diameter and 500 nm in length. The hydrophilic properties of the anodized surfaces were significantly improved. The adsorbed rhBMP-2 loaded on the nonanodized surfaces and lyophilized showed spherical particle morphology. However, the adsorbed rhBMP-2 showed a dispersed pattern over the anodized surfaces. The velocity of the rhBMP-2 released from the surfaces was measured to determine if the anodized surface can improve in delivery efficiency. The results showed that the release velocity of the rhBMP-2 from the anodized surfaces was sustained when compared with that of the nonanodized surfaces. In addition, the rhBMP-2 released from the surface was found to be bioactive according to the alkaline phosphatase activity and the level of calcium mineral deposition. These results suggest that the TiO(2) nanotubular structure formed by anodizing is a promising configuration for sustained rhBMP-2 delivery.

No abstract

No abstract

The purpose of this study was to fabricate and characterize nanotubular structure on machined titanium (MA) and resorbable blast media (RBM) treated titanium by anodizing. The anodized MA and RBM were characterized with scanning electron microscopy, transmission electron microscopy, X-ray diffraction, energy disperse spectra, X-ray photoelectron spectra, and nano-indentation and scratch test. Highly ordered nanotubular layers of individually 100 nm in diameter and 500 nm in length approximately were formed regardless of the substrates. The nanotubular layers consisted mainly of amorphous TiO(2) with trace fluorine. The nanotubular surfaces on both the substrates significantly reduced water contact angles and elastic modulus compared with those prior to anodizing. The anodizing treatment significantly increased the surface roughness of the smooth MA, but significantly decreased the surface roughness of the roughened RBM. The critical delamination forces of the nanotubular layer were not obtained due to the limitation of surface roughness. The anodized RBM consisted of a nano-micro porous graded structure, or a nanotubular amorphous fluoride containing TiO(2) layer on top of micro-roughened titanium surface, which is expected to significantly improve the surface area that can be used to deliver drugs and growth factors and alleviate the interfacial elastic modulus mismatch as to enhance osseointegration when compared with conventional dental and orthopedic implant devices with smooth or acid etched surface.

No abstract

No abstract

PURPOSEThe aim of this study was to evaluate antibacterial activity and osteoblast-like cell viability according to the ratio of titanium nitride and zirconium nitride coating on commercially pure titanium using an arc ion plating system.MATERIALS AND METHODSPolished titanium surfaces were used as controls. Surface topography was observed by scanning electron microscopy, and surface roughness was measured using a two-dimensional contact stylus profilometer. Antibacterial activity was evaluated against Streptococcus mutans and Porphyromonas gingivalis with the colony-forming unit assay. Cell compatibility, mRNA expression, and morphology related to human osteoblast-like cells (MG-63) on the coated specimens were determined by the XTT assay and reverse transcriptase-polymerase chain reaction.RESULTSThe number of S. mutans colonies on the TiN, ZrN and (Ti1-xZrx)N coated surface decreased significantly compared to those on the non-coated titanium surface (P<0.05).CONCLUSIONThe number of P. gingivalis colonies on all surfaces showed no significant differences. TiN, ZrN and (Ti1-xZrx)N coated titanium showed antibacterial activity against S. mutans related to initial biofilm formation but not P. gingivalis associated with advanced periimplantitis, and did not influence osteoblast-like cell viability.