A supercapacitor electrode is fabricated with Co0.85Se hollow nanowires (HNW) array, which is synthesized by wet chemical hydrothermal selenization of initially grown cobalt hydroxyl carbonate nanowires on conductive CFP. The dense self-organized morphology of Co0.85Se HNWs is revealed by scanning/transmission electron microscopy. The as-synthesized Co0.85Se HNWs possess high pseudocapacitive property with high capacitance retention and high durability. The areal capacitance value is seen to vary from 929.5 to 600 mF cm(-2) (60% retention) as the current density is increased from 1 to 15 mA cm(-2), an increase of a factor of 15. Based on mass loading, this corresponds to a very high gravimetric capacitance of 674 (for 2 mA cm(-2) or 1.48 Ag(-1)) and 444 Fg(1-) (for 15 mA cm(-2) or 11 A g(-1)) in a full-cell configuration with the Co0.85Se HNWs as cathode and activated carbon as anode (asymmetric configuration) promising results are obtained.
Lithium ion hybrid capacitors (Li-HECs) have attracted significant attention for use in next generation advanced energy storage technologies to satisfy the demand of both high power density as well as energy density. Herein we demonstrate the use of very high surface area 3D carbon cuboids synthesized from a metal-organic framework (MOF) as a cathode material with Li₄Ti₅O₁₂ as the anode for high performance Li-HECs. The energy density of the cell is ∼65 W h kg(-1) which is significantly higher than that achievable with commercially available activated carbon (∼36 W h kg(-1)) and a symmetric supercapacitor based on the same MOF-derived carbon (MOF-DC ∼20 W h kg(-1)). The MOF-DC/Li₄Ti₅O₁₂ Li-HEC assembly also shows good cyclic performance with ∼82% of the initial value (∼25 W h kg(-1)) retained after 10,000 galvanostatic cycles under high rate cyclic conditions. This result clearly indicates that MOF-DC is a very promising candidate for future P-HEVs in a Li-HEC configuration.
Direct assembling of N-graphene, i.e. nitrogen doped graphene, in a controllable manner was achieved using microwave plasmas at atmospheric pressure conditions. The synthesis is accomplished via a single step using ethanol and ammonia as carbon and nitrogen precursors. Tailoring of the high-energy density plasma environment results in a selective synthesis of N-graphene (~0.4% doping level) in a narrow range of externally controlled operational conditions, i.e. precursor and background gas fluxes, plasma reactor design and microwave power. Applying infrared (IR) and ultraviolet (UV) irradiation to the flow of free-standing sheets in the post-plasma zone carries out changes in the percentage of sp2, the N doping type and the oxygen functionalities. X-ray photoelectron spectroscopy (XPS) revealed the relative extension of the graphene sheets π-system and the type of nitrogen chemical functions present in the lattice structure. Scanning Electron microscopy (SEM), Transmission Electron microscopy (TEM) and Raman spectroscopy were applied to determine morphological and structural characteristics of the sheets. Optical emission and FT-IR spectroscopy were applied for characterization of the high-energy density plasma environment and outlet gas stream. Electrochemical measurements were also performed to elucidate the electrochemical behavior of NG for supercapacitor applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.