The contraction stress generated during the photopolymerization of resin dental composites is the major disadvantage. The water sorption in the oral environment should counteract the contraction stress. The purpose was to evaluate the influence of the water sorption of composite materials on polymerization shrinkage stress generated at the restoration-tooth interface. The following materials were tested: Filtek Ultimate, Gradia Direct LoFlo, Heliomolar Flow, Tetric EvoCeram, Tetric EvoCeram Bulk Fill, Tetric EvoFlow, Tetric EvoFlow Bulk Fill, X-tra Base, Venus BulkFil, and Ceram.X One. The shrinkage stress was measured immediately after curing and after: 0.5 h, 24 h, 72 h, 96 h, 168 h, 240 h, 336 h, 504 h, 672 h, and 1344 h by means of photoelastic study. Moreover, water sorption and solubility were evaluated. Material samples were weighted on scale in time intervals to measure the water absorbency and the dynamic of this process. The tested materials during polymerization generated shrinkage stresses ranging from 6.3 MPa to 12.5 MPa. Upon water conditioning (56 days), the decrease in shrinkage strain (not less than 48%) was observed. The decrease in value stress in time is material-dependent.
The aim of the study was to evaluate antibacterial activity of composite materials modified with calcium fluoride against cariogenic bacteria S. mutans and L. acidophilus. One commercially available conventional light-curing composite material containing fluoride ions (F2) and two commercially available flowable light-curing composite materials (Flow Art and X-Flow) modified with 1.5, 2.5, and 5.0 wt% anhydrous calcium fluoride addition were used in the study. Composite material samples were incubated in 0.95% NaCl at 35°C for 3 days; then dilution series of S. mutans and L. acidophilus strains were made from the eluates. Bacteria dilutions were cultivated on media afterwards. Colony-forming unit per 1 mL of solution (CFU/mL) was calculated. Composite materials modified with calcium fluoride highly reduced (p < 0.001) bacteria growth compared to commercially available composite materials containing fluoride compounds. The greatest reduction in bacteria growth was observed for composite materials modified with 1.5% wt. CaF2. All three tested composite materials showed statistically greater antibacterial activity against L. acidophilus than against S. mutans.
Ion-releasing polymeric restorative materials seem to be promising solutions, due to their possible anticaries effect. However, acid functional groups (monomers) and glass filler increase hydrophilicity and, supposedly, water sorption. The purpose of the study was to evaluate the influence of water sorption of polymeric materials on the stress state at the restoration-tooth interface. Beautifil Bulk Fill Flow, Beautifil Flow Plus F00, Beautifil Flow F02, Dyract eXtra, Compoglass Flow, Ionosit, Glasiosite, TwinkiStar, Ionolux and Fuji II LC were used for the study. The stress state was measured using photoelastic analysis after: 0.5, 24, 72, 96, 168, 240, 336, 504, 672, 1344 and 2016 h. Moreover, water sorption, solubility and absorption dynamic were assessed. The water sorption, solubility and absorption dynamic of ion-releasing restorative materials are material dependent properties. The overall results indicated that the tested restorative materials showed significant stress decrease. The total reduction in contraction stress and water expansion stress was not observed for materials with low value of water sorption (Beautifil Bulk Fill, Dyract eXtra, Glasionosit and Twinky Star). The photoelastic method turned out to be inadequate to evaluate stress changes of resin modified glass-ionomer cement (RMGI, Fuji II LC and Ionolux).
There is no consensus on the antibacterial activity of dentin bonding systems (DBS). Many study models have been used to evaluate the antimicrobial activity of dental materials. In this study, a novel detection method, flow cytometry, was introduced. It allows for evaluation of the antibacterial activity of DBS, based on assessment of the disruption of the bacterial physical membrane induced by DBS. The aim of the study was to evaluate the antibacterial properties of selected dentin bonding systems against Streptococcus mutans. The highest antibacterial activity against S. mutans was observed for Adhese Universal (99.68% dead cells) and was comparable to that of Prime&Bond Universal, OptiBond Universal, or Clearfil Universal Bond Quick (p > 0.05). The lowest activity of all tested systems was displayed by the multi-mode adhesive, Universal Bond (12.68% dead bacteria cells), followed by the self-etch adhesive, OptiBond FL (15.58% dead bacteria cells). The present study showed that in the case of two-component DBS, the primer exhibited higher antimicrobial activity than the adhesive (or bond) itself.
The aim of this paper was to identify and to assess in semi-quantified way the release of different ions from composite and compomer restorative materials subjected to 0.9% NaCl solution, which simulates the environment of the human body. In the present study, the number of ions (Al, Ag, Ba, Sr, Ti) released from dental fillings over time (one week, one month and 3 months), in different temperatures (23°C, 37°C) and depending on the materials applied (unmodified/modified with nanosilver) was investigated. The results suggest that nanosilver addition influences directly on the process of metal ion releasing into 0.9% NaCl solution. The increase in the number of counts of metal ions was observed in the solutions in which samples modified with nanosilver were kept. Higher amount of metal ion release was observed for composite samples rather than for compomer materials. The study revealed that in general the number of released metal ions increases with the time of storage (for metal ions: Ti, Ba, Sr) and at higher temperature (Ag, Ti, Ba). Reverse tendency observed for silver ion release versus incubation time may be caused by the process of silver adsorption, which takes place on the surface of analyzed material and test-tube walls, where samples were incubated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.