Alloy 709 was oxidized at 700 °C for 500 h in a steam environment. A microstructural analysis of the oxide scale is reported. Modern techniques of advanced electron microscopy were used to characterize the morphology of the oxide scale and recognize its single components. The material developed a complex, multilayered oxide scale. The outermost layer consisting of Fe2O3. Fe2NiO4 tI28 spinel was detected underneath. An internal oxidation zone is present in the innermost layer. High quality SEM-EDS maps give insight into a larger area of the oxide scale at a relatively low magnification.

The modern power generation industry needs materials able to withstand severe conditions, such as high temperatures, steam pressure, and an aggressive environment, to create more electric power out of a decreasing amount of fuel. Therefore, new metallic materials are continuously being developed. In order to gain knowledge about modern materials, the investigation of high Cr and Ni austenitic steel oxidized in 100% steam at 700 °C for 500 h was performed. The morphology, the phase composition, and the chemical composition of the oxidation products were investigated through methods of advanced electron microscopy techniques. Moreover, precipitates present in bulk material were identified. The material developed a continuous and complex oxide scale, consisting of Fe2O3, Cr2O3, and spinel phases. Very fine MX, fine ε-Cu, and M23C6 precipitates were found in the bulk material. The creation of iron oxide is induced due to the coarse grain size of the material. Cr2O3 forms due to the internal oxidation process.