The origins for abrupt adhesion loss at a critical relative humidity (RH) for polymeric adhesives bonded to inorganic surfaces have been explored using a model poly(methyl methacrylate) (PMMA) film on glass. The interfacial and bulk water concentrations within the polymer film as a function of D 2O partial pressure were quantified using neutron reflectivity. Adhesion strength of these PMMA/SiO 2 interfaces under the same conditions was quantified using a shaft loaded blister test. A drop in adhesion strength was observed at a critical RH, and at this same RH, a discontinuity in the bulk moisture concentration occurred. The moisture concentration near the interface was higher than that in the bulk PMMA, and at the critical RH, the breadth of the interfacial water concentration distribution as a function of distance from the SiO 2/PMMA interface increased dramatically. We propose a mechanism for loss of adhesion at a critical RH based upon the interplay between bulk swelling induced stress and weakening of the interfacial bond by moisture accumulation at the PMMA/SiO 2 interface.
TiO2 thin film based, chemiresistive sensors for NO2 gas which operate at room temperature under ultraviolet (UV) illumination have been demonstrated in this work. The rf-sputter deposited and post-annealed TiO2 thin films have been characterized by atomic force microscopy, X-ray photoelectron spectroscopy, and X-ray diffraction to obtain surface morphology, chemical state, and crystal structure, respectively. UV-vis absorption spectroscopy and Tauc plots show the optical properties of the TiO2 films. Under UV illumination, the NO2 sensing performance of the TiO2 films shows a reversible change in resistance at room-temperature. The observed change in electrical resistivity can be explained by the modulation of surface-adsorbed oxygen. This work is the first demonstration of a facile TiO2 sensor for NO2 analyte that operates at room-temperature under UV illumination.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.