Highly dispersed uniform silver nanoparticles were prepared by reducing silver diamine ions [Ag(NH3)2]+ with D-glucose in the presence of a stabilizing agent. Along with the nature of the dispersing agent, the pH and the temperature of the reaction had the most pronounced effect on the reduction rate, the nucleation of the metallic phase, and ultimately the size and dispersion of the resulting particles. Through suitable manipulations of these parameters, it was possible to prepare uniform Ag nanoparticles ranging in size from 30 to 120 nm. A rapid and complete reduction of the silver species was possible only at elevated pH and temperatures above 50 °C. The reduction of silver diamine ions in these conditions caused the complete cleavage of the C–C bond, resulting in the release of 12 electrons per molecule of D-glucose. It was also found that the addition of ammonia to an already acidified silver nitrate solution leads to the formation of a much more stable and safe-to-handle diamine complex.

An environmentally friendly route to prepare stable concentrated aqueous dispersions of silver nanoparticles is described. It was found that Arabic gum, a well known stabilizing agent, can also rapidly and completely reduce Ag2O to metallic silver in alkaline solutions (pH > 12.0) and elevated temperature (65 °C). The average size of the silver nanoparticles could be tailored from 10 to 30 nm by varying the experimental conditions. By hydrolyzing either enzymatically or chemically the polysaccharide, it was possible to isolate dispersed silver nanoparticles suitable for both biological and printable electronics applications. For the latter purpose, concentrated dispersions of silver particles were prepared and used for depositing thin uniform layers, which could be sintered into conductive films at low temperatures.

Inks containing silver nanoparticles of 12 nm, 80 nm, and a 15%/85% mixture of the two sizes were used to evaluate the effect of particle size and size distribution on the electrical properties of sintered films. The silver layers deposited with a "drop-on-demand" inkjet printer were heated at temperatures ranging from 125 to 200 C. The small particles formed less resistive films at 125 C, while the larger ones provided better electrical conductivity above 150 C. The inks containing mixed small and large particles yielded the most conductive silver films over the entire investigated temperature range. A mechanism explaining these results is proposed based on the evolution of film microstructure with temperature.