Al/Cu dissimilar joining is a key technology for reducing the weight and cost of electrical components. In this study, the dissimilar friction stir lap welding (FSLW) of a Ni-containing Al alloy to pure Cu was performed, and the effects of the addition of Ni on the weld strength and interfacial microstructure were examined. A thin intermetallic compound (IMC) layer was observed at the Al/Cu weld interface produced by FSLW. The addition of 3 at.% Ni effectively improved the weld strength, although the thickness of the IMC layer increased. The IMC layer formed at the Al/Cu interface without Ni comprised CuAl2 and Cu9Al4 from the pure Al side. In contrast, the IMC layer formed with 3 at.% Ni consisted of (Ni,Cu)Al, CuAl, and Cu9Al4 from the Al side. The addition of Ni eliminated the weak CuAl2/Cu9Al4 interface, thereby improving the weld strength. The results of this study suggest that the strength of the Al/Cu weld can be effectively improved by the thinning of the IMC layer caused by FSLW and the change in interfacial microstructure caused by Ni addition.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.