The packing of cellulose nanocrystals (CNC) in the anisotropic chiral nematic phase has been investigated over a wide concentration range by small-angle X-ray scattering (SAXS) and laser diffraction. The average separation distance between the CNCs and the average pitch of the chiral nematic phase have been determined over the entire isotropic-anisotropic biphasic region. The average separation distances range from 51 nm, at the onset of the anisotropic phase formation, to 25 nm above 6 vol % (fully liquid crystalline phase) whereas the average pitch varies from ≈15 μm down to ≈2 μm as ϕ increases from 2.5 up to 6.5 vol %. Using the cholesteric order, we determine that the twist angle between neighboring CNCs increases from about 1° up to 4° as ϕ increases from 2.5 up to 6.5 vol %. The dependence of the twisting on the volume fraction was related to the increase in the magnitude of the repulsive interactions between the charged rods as the average separation distance decreases.
We show that unidirectional freezing of nanocellulose dispersions produces cellular foams with high alignment of the rod-like nanoparticles in the freezing direction. Quantification of the alignment in the long direction of the tubular pores with X-ray diffraction shows high orientation of cellulose nanofibrils (CNF) and cellulose nanocrystals (CNC) at particle concentrations above 0.2 wt % (CNC) and 0.08 wt % (CNF). Aggregation of CNF by pH decrease or addition of salt significantly reduces the particle orientation; in contrast, exceeding the concentration where particles gel by mobility constraints had a relatively small effect on the orientation. The dense nanocellulose network formed by directional freezing was sufficiently strong to resist melting. The formed hydrogels were birefringent and displayed anisotropic laser diffraction patterns, suggesting preserved nanocellulose alignment and cellular structure. Nondirectional freezing of the hydrogels followed by sublimation generates foams with a pore structure and nanocellulose alignment resembling the structure of the initial directional freezing.
Designing engineering materials with high stiffness and high toughness is challenging as stiff materials tend to be brittle. Many biological materials realize this objective through multiscale (i.e., atomic‐ to macroscale) mechanisms that are extremely difficult to replicate in synthetic materials. Inspired from the architecture of such biological structures, we here present flow‐assisted organization and assembly of renewable native cellulose nanofibrils (CNFs), which yields highly anisotropic biofibers characterized by a unique combination of high strength (1010 MPa), high toughness (62 MJ m−3) and high stiffness (57 GPa). We observed that properties of the fibers are primarily governed by specific ion characteristics such as hydration enthalpy and polarizability. A fundamental facet of this study is thus to elucidate the role of specific anion binding following the Hofmeister series on the mechanical properties of wet fibrillar networks, and link this to the differences in properties of dry nanostructured fibers. This knowledge is useful for rational design of nanomaterials and is critical for validation of specific ion effect theories. The bioinspired assembly demonstrated here is relevant example for designing high‐performance materials with absolute structural control.
Nanocellulose-based lightweight foams are promising alternatives to fossil-based insulation materials for energy-efficient buildings. The properties of cellulose-based materials are strongly influenced by moisture and there is a need to assess and better understand how the thermal conductivity of nanocellulose-based foams depends on the relative humidity and temperature. Here, we report a customized setup for measuring the thermal conductivity of hydrophilic materials under controlled temperature and relative humidity conditions. The thermal conductivity of isotropic foams based on cellulose nanofibrils and a nonionic polyoxamer, and an expanded polystyrene foam was measured over a wide range of temperatures and relative humidity. We show that a previously developed model is unable to capture the strong relative humidity dependence of the thermal conductivity of the hygroscopic, low-density nanocellulose-and nonionic polyoxamer-based foam. Analysis of the moisture uptake and moisture transport was used to develop an empirical model that takes into consideration the moisture content and the wet density of the investigated foam. The new empirical model could predict the thermal conductivity of a foam with a similar composition but almost 3 times higher density.Accurate measurements of the thermal conductivity at controlled temperature and relative humidity and availability of simple models to better predict the thermal conductivity of hygroscopic, low-density foams are necessary for the development of nanocellulose-based insulation materials.
We have followed the structural evolution during evaporation-induced self-assembly of sulfonated cellulose nanocrystal (CNC) in the presence of H+ and Li+ counterions by small-angle X-ray scattering. Drying of CNC-H dispersions results in ordered films that could not be readily redispersed, while the CNC-Li films were disordered and prone to reswelling and redispersion. The scaling of the separation distance (d) between CNC particles and the particle concentration (c) shows that the CNC-H dispersions display a unidimensional contraction of the nematic structure (d ∝ c –1) during drying, while the CNC-Li dispersions consolidate isotropically (d ∝ c –1/3), which is characteristic for hydrogels with no preferential orientation. Temporal evolution of the structure factor and complementary dynamic light-scattering measurements show that CNC-Li is more aggregated than CNC-H during evaporation-induced assembly. Insights on the structural evolution during CNC assembly and redispersion can promote development of novel and optimized processing routes of nanocellulose-based materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.