PURPOSEThis in vitro study intended to investigate the mechanical and thermal characteristics of Valplast, and of polymethyl methacrylate denture base resin in which different esthetic fibers (E-glass, nylon 6 or nylon 6.6) were added.MATERIALS AND METHODSFive groups were formed: control (PMMA), PMMA-E glass, PMMA-nylon 6, PMMA-nylon 6.6 and Valplast resin. For the transverse strength test the specimens were prepared in accordance with ANSI/ADA specification No.12, and for the impact test ASTM D-256 standard were used. With the intent to evaluate the properties of transverse strength, the three-point bending (n=7) test instrument (Lloyd NK5, Lloyd Instruments Ltd, Fareham Hampshire, UK) was used at 5 mm/min. A Dynatup 9250 HV (Instron, UK) device was employed for the impact strength (n=7). All of the resin samples were tested by using thermo-mechanical analysis (Shimadzu TMA 50, Shimadzu, Japan). The data were analyzed by Kruskal-Wallis and Tukey tests for pairwise comparisons of the groups at the 0.05 level of significance.RESULTSIn all mechanical tests, the highest values were observed in Valplast group (transverse strength: 117.22 ± 37.80 MPa, maximum deflection: 27.55 ± 1.48 mm, impact strength: 0.76 ± 0.03 kN). Upon examining the thermo-mechanical analysis data, it was seen that the E value of the control sample was 8.08 MPa, higher than that of the all other samples.CONCLUSIONAlthough Valplast denture material has good mechanical strength, its elastic modulus is not high enough to meet the standard of PMMA materials.

PURPOSEIn this study, three bioceramic materials, [IPS Empress CAD (Ivoclar), IPS e.max CAD (Ivoclar), and Lava Ultimate CAD (3M ESPE)] were treated with three commercial mouthrinses [Listerine, Tantum Verde, and Klorhex]; and changes in colour reflectance and surface roughness values were then quantitatively assessed.MATERIALS AND METHODSOne hundred and twenty ceramic samples, with dimensions of 2 × 12 × 14 mm, were prepared and divided into nine sample groups, except three control samples. The samples were immersed in the mouthrinse solutions for 120 hrs, and changes in colour reflectance and surface roughness values were measured by UV light spectrophotometry (Vita Easyshade; VITA Zahnfabrik) and by profilometer device (MitutoyoSurftest SJ-301), respectively. The change of surface roughness was inspected by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM).RESULTSThere was a positive correlation between the ΔE and increase in the surface roughness. Two of the ceramic materials, IPS Empress and Lava Ultimate, were affected significantly by the treatment of the mouthrinse solutions (P<.05). The most affecting solution was Tantum Verde and the most affected material was Lava Ultimate. As expected, the most resistant material to ΔE and chemical corrosion was IPS e max CAD among the materials used.CONCLUSIONThis work implied that mouthrinse with lower alcohol content had less deteriorating effect on colour and on the surface morphology of the bioceramic materials.

In the present study, tensile bond strength between an acrylic resin and a resilient denture liner, Molloplast B, was studied. To enhance the bonding capacity between these materials, acrylic resin surface was modified using ethyl methacrylate, iso-butyl methacrylate or tert-butyl methacrylate monomers. Changes on the modified surfaces were investigated by Fourier transform infrared spectroscopy with attenuated total reflectance. Only the modifications by isobutyl methacrylate application appeared to have an increasing effect on the tensile bond strength value. Ethyl methacrylate and tert-butyl methacrylate, however, had a lowering effect on this value.

Thisin vitrostudy investigated the mechanical and structural characteristics of lignin-added PMMA resin composites at concentrations of 1, 3, and 5% by weight. Four sample groups were formed. For the transverse strength test, the specimens were prepared in accordance with ANSI/ADA specification number 12, and for the impact test ASTM D-256 standards were used. With the intent to evaluate the properties of transverse strength, the three-point bending (n=10) test instrument (Lloyd NK5, Lloyd Instruments Ltd., Fareham, Hampshire, UK) was used at 5 mm/min. A Dynatup 9250 HV (Instron, UK) device was employed for the impact strength measurements (n=10). All resin samples were tested by using a thermomechanical analyzer (Shimadzu TMA 50, Shimadzu, Japan). Mechanical tests revealed that, although the control group was found to have the value of highest transverse strength, the highest impact strength was observed in the PMMA-L-1 group. Upon examining the thermomechanical analysis data, it could be seen that theEvalue of the control sample was higher than that of all the other samples. Adding lignin powder into PMMA performs plasticizer effect on resin matrix.

No abstract

No abstract

No abstract

No abstract