Summary: Hydrogenated acrylonitrile butadiene rubber (HNBR) was melt compounded with montmorillonite (MMT) and organophilic modified MMTs prior to sulfur curing. In contrast to the micro‐composite formation resulting from the compounding of the HNBR and pristine MMT, the modified MMTs (i.e., octadecylamine: MMT‐ODA, octadecyltrimethylamine: MMT‐ODTMA, methyltallow‐bis(2‐hydroxyethyl) quaternary ammonium: MMT‐MTH intercalants) produced nanocomposites. It was found that the organoclay with primary amine intercalant (cf. MMT‐ODA) gave confined structures along with the exfoliated/intercalated structures. This was traced to its reactivity with the curatives. By contrast, the organoclays containing less reactive quaternary ammonium compounds (cf. MMT‐ODTMA, MMT‐MTH) were exfoliated and intercalated based on X‐ray diffraction (XRD) and transmission electron microscopy (TEM) results. The hydroxyl functional groups of the MMT‐MTH supported the clay dispersion. The better adhesion between MMT‐MTH and HNBR was explained by hydrogen bonding between the hydroxyl groups of the intercalant and the acrylonitrile group of the HNBR matrix. This HNBR/MMT‐MTH nanocomposite showed the best mechanical properties as verified by tensile mechanical tests and dynamic mechanical thermal analysis (DMTA). The high tensile strength along with the high elongation at break for the rubber nanocomposites were attributed to the ability of the ‘clay network’ to dissipate the input energy upon uniaxial loading.
Natural rubber (NR), polyurethane rubber (PUR), and NR/PUR-based nanocomposites were produced from the related latices by adding a pristine synthetic layered silicate (LS; sodium fluorohectorite) in 10 parts per hundred parts rubber (phr). The dispersion of the LS latices in the composite was studied by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Further information on the rubber/LS interaction was received from Fourier transform infrared spectroscopy (FTIR) and dynamic mechanical thermal analysis (DMTA). Tensile and tear tests were used to characterize the performance of the rubber nanocomposites. It was found that LS is more compatible and thus better intercalated by PUR than by NR. Further, LS was preferably located in the PUR phase in the blends, which exhibited excellent mechanical properties despite the incompatibility between NR and PUR. Nano-reinforcement was best reflected in stiffness-and strength-related properties of the rubber composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.