8 mol% yttria‐stabilized zirconia (8YSZ) is an extensively studied solid electrolyte. But there is no consistency in the reported ionic conductivity values of 8YSZ thin films. Interfacial segregation in YSZ thin films can affect its ionic conductivity by locally altering the surface chemistry. This article presents the effects of annealing temperature and film thickness on free surface yttria segregation behavior in 8YSZ thin film by Angle Resolved XPS and its influence on the ionic conductivity of sputtered 8YSZ thin films. Surface yttria concentration of about 32, 20, and 9 mol% have been found in 40 nm 8YSZ films annealed at 1273, 1173, and 1073 K, respectively. Yttria segregation is found to increase with increase in annealing temperature and film thickness. Ionic conductivities of 0.23, 0.16, and 0.08 Scm−1 are observed at 923 K for 40 nm 8YSZ films annealed at 1073, 1173, and 1273 K, respectively. The decrease in conductivity with increase in annealing temperature is attributed to the increased yttria segregation with annealing. Neither segregation nor film thickness is found to affect the activation energy of oxygen ion conduction. Target purity is found to play a key role in determining free surface yttria segregation in 8YSZ thin films.

Downscaling of yttria stabilized zirconia (YSZ) based electrochemical devices and gate oxide layers requires successful pattern transfer on YSZ thin films. Among a number of techniques available to transfer patterns to a material, reactive ion etching has the capability to offer high resolution, easily controllable, tunable anisotropic/isotropic pattern transfer for batch processing. This work reports inductively coupled reactive ion etching studies on sputtered YSZ thin films in fluorine and chlorine based plasmas and their etch chemistry analyses using x-ray photoelectron spectroscopy. Etching in SF6 plasma gives an etch rate of 7 nm/min chiefly through physical etching process. For same process parameters, in Cl2 and BCl3 plasmas, YSZ etch rate is 17 nm/min and 45 nm/min, respectively. Increased etch rate in BCl3 plasma is attributed to its oxygen scavenging property synergetic with other chemical and physical etch pathways. BCl3 etched YSZ films show residue-free and smooth surface. The surface atomic concentration ratio of Zr/Y in BCl3 etched films is closer to as-annealed YSZ thin films. On the other hand, Cl2 etched films show surface yttrium enrichment. Selectivity ratio of YSZ over silicon (Si), silicon dioxide (SiO2) and silicon nitride (Si3N4) are 1:2.7, 1:1, and 1:0.75, respectively, in BCl3 plasma. YSZ etch rate increases to 53 nm/min when nonoxygen supplying carrier wafer like Si3N4 is used.

No abstract