An enhanced Cu-based friction material was prepared by the powder metallurgy techniques and proposed for use in the dry clutch system. The friction characteristics and wear rate of this friction material sliding against 65Mn steel are obtained using Universal Material Tester-5. The friction pairs were subjected to two operating variables, which are sliding speed and temperature. The effect of these variables during the engagement process of the friction pairs is investigated. Knowing the normal applied force and dimension of the clutch disc, the dynamic friction coefficient was translated to friction torque capacity with time. It was found that instability can be excited at low operational conditions when the resulting friction coefficient is high. At 25 ℃, the dynamic friction torque oscillates with time likewise at 400 ℃. Generally, a more stable friction torque is obtained when the sliding speed is varied compared to varying the temperatures. Moreover, the influence of the operating temperatures and sliding speeds on thermal buckling and thermoelastic instability of the friction disc is the second consideration in this work. The onset of thermoelastic instability occurs when the sliding speed exceeded 200 r/min and the results for the growth rate of hot spots were found to agree well with the critical speed of the system. Also, thermal buckling was highly dependent on the temperature difference between the inner and outer radius of the friction disc.
Studies have shown that reinforced paper-based friction material with 600 µm carbon fiber length possesses a high dynamic friction coefficient but is subjected to abrasive wear during sliding contact. This work is devoted to further investigate the effect of operating variables on this friction material subjected to high operating conditions. A pin-on-disc test was carried out to determine the tribological behavior of this friction material sliding against 65Mn steel. The friction and wear rate results from measurements were discussed. The highest friction value of about 0.3 was obtained by varying the applied load at 120 N while the lowest friction value close to 0.02 was obtained when the sliding speed was 0.026 m/s. Increasing the sliding speed above 0.30 m/s caused constant temperature (175 °C) to fluctuate due to high friction heat generation on the sliding surface. The highest wear rate was 1.42 × 10−15m3/Nm by varying the sliding speed at 1.31 m/s. In contrast, the lowest wear rate was 2.1 × 10−16m3/Nm when the temperature was at 400 °C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.