ABSTRACT:The shear and extensional viscosities of a polypropylene resin were studied using a capillary rheometer and capillary dies of 1-mm diameter and length of 10, 20, and 30 mm. Melt temperatures at 190, 205, and 220°C and shear rates between 100 and 5000 s Ϫ1 were used. At the highest shear rate a visible melt fracture was observed. An equation relating the pressure drop and die length was derived with consideration of pressure effects on melt viscosities and the end effect. After the correction for pressure effects the true wall shear stress and end effect at zero pressure were calculated. The end effect showed a critical stress of melt fracture around 10 5 Pa, and increased rapidly when shear stress increased above the critical stress. From shear stress the shear viscosity was calculated, and a power law behavior was observed. Extensional viscosity was calculated from the end effect and showed a decreasing trend when strain rate increased. After time-temperature superposition shift shear viscosity data correlated well, but an upward trend was observed in extensional viscosity when melt fracture occurred. Die swell ratio at different temperatures can be plotted as a function of wall shear stress and was higher for shorter dies.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.