The COVID-19 pandemic has clearly shown the importance of developing advanced protective equipment, and new antiviral fabrics for the protection and prevention of life-threatening viral diseases are needed. In this study, selenium nanoparticles (SeNPs) were combined with polyester fabrics using printing technique to obtain multifunctional properties, including combined antiviral and antibacterial activities as well as coloring. The properties of the printed polyester fabrics with SeNPs were estimated, including tensile strength and color fastness. Characterization of the SeNPs was carried out using TEM and SEM. The results of the analysis showed good uniformity and stability of the particles with sizes range from 40–60 nm and 40–80 nm for SeNPs 25 mM and 50 mM, respectively, as well as uniform coating of the SeNPs on the fabric. In addition, the SeNPs—printed polyester fabric exhibited high disinfection activity against severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2) with an inhibition percentage of 87.5%. Moreover, a toxicity test of the resulting printed fabric revealed low cytotoxicity against the HFB4 cell line. In contrast, the treated fabric under study showed excellent killing potentiality against Gram-positive bacteria (Bacillus cereus) and Gram-negative bacteria (Pseudomonas aeruginosa, Salmonella typhi, and Escherichia coli). This multifunctional fabric has high potential for use in protective clothing applications by providing passive and active protection pathways.
In this study, we developed a new approach for depositing selenium nanoparticles (SeNPs) into polypropylene (PP) fabrics via a one-step process under hydrothermal conditions by using an IR-dyeing machine to incorporate several functionalities, mainly coloration, antibacterial activity and ultraviolet (UV) protection. The formation, size distribution, and dispersion of the SeNPs were determined using X-ray diffraction (XRD), ultraviolet-visible (UV/Vis), transmission electron microscopy (TEM) and the color strength, fastness, antibacterial properties, and UV protection of the treated fabrics were also explored. The UV-Vis spectra and TEM analysis confirmed the synthesis of spherical well-dispersed SeNPs and the XRD analysis showed the successful deposition of SeNPs into PP fabrics. The obtained results demonstrate that the SeNPs-PP fabrics is accompanied by a noticeable enhancement in measurements of color strength, fastness, and UV-protection factor (UPF), as well as excellent antibacterial activity. Viability studies showed that SeNPs-PP fabrics are non-toxic against wi-38cell line. In addition, the treated SeNPs-PP fabrics showed an increase in conductivity. The obtained multifunctional fabrics are promising for many industrial applications such as the new generation of curtains, medical fabrics, and even automotive interior parts.
Nanoparticles (NPs) have attracted great interest in various fields owing to their antimicrobial activity; however, the use of NPs as fungicides on plants has not been sufficiently investigated. In this study, the antifungal activities of sulfur nanoparticles (S-NPs) and copper nanoparticles (Cu-NPs) prepared by a green method were evaluated against Botrytis cinerea and Sclerotinia sclerotiorum. The formation of NPs was confirmed by transmission electron microscopy (TEM) and X-ray diffraction analysis (XRD). The antifungal activities of NPs (5–100 µg/mL), CuSO4 (4000 µg/mL), and micro sulfur (MS) were compared to those of the recommended chemical fungicide Topsin-M 70 WP at a dose of 1000 µg/mL. They were evaluated in vitro and then in vivo at different temperatures (10 and 20 °C) on cucumber (Cucumis sativus) fruits. The total phenolic content (TPC) and total soluble solids (TSS) were determined to study the effects of various treatments on the shelf life of cucumber fruits, compared to untreated cucumber as a positive control. The diameters of S-NPs and Cu-NPs ranged from 10 to 50 nm, and 2 to 12 nm, respectively. The results revealed that S-NPs exhibited the highest antifungal activity, followed by Cu-NPs. However, CuSO4 showed the lowest antifungal activity among all treatments. The antifungal activity of the prepared NPs increased with the increase in NP concentration, while the fungal growth was less at low temperature. The cytotoxicity of the prepared NPs was evaluated against the WI-38 and Vero cell lines in order to assess their applicability and sustainability. S-NPs caused less cytotoxicity than Cu-NPs.
Because of its low critical temperature and pressure levels, supercritical carbon dioxide (scCO2) is the most widely used supercritical fluid in the supercritical fluid extraction (SFE) technique. Alizarin was extracted from madder roots (Rubia tinctorum) using scCO2 under different conditions of co-solvent ratio (0–50%), temperature (45–95 °C), pressure (150–250 bar), extraction time (15–120 min), and flow rate (5–9 mL/min). Based on alizarin recovery and minimization of environmental risk, the optimum conditions were determined. SFE was optimum at 90% CO2:10% methanol (Me), 65 °C, 250 bar, 45 min, and 9 mL/min. The alizarin recovery, and its content in R. tinctorum extract (RE) under the optimum conditions were 1.34 g/kg roots, and 6.42%, respectively. Using conventional dyeing methods, wool fabrics were dyed with RE at different concentrations (2–6%). Various types of mordants were also used in the dyeing process, including chemical and bio-mordants. Color and fastness properties of dyed wool fabrics were evaluated based on RE concentration and mordant type. A higher RE concentration and the use of mordants, specifically Punica granatum (P. granatum) peels, increased the color characteristics. RE and dyed fabrics exhibited good antibacterial activity against the tested bacterial strains, especially Pseudomonas aeruginosa and Escherichia coli.
It has become increasingly popular to replace chemically synthesized compounds with natural counterparts mostly found in natural sources, such as natural pigments. The conventional extraction processes for these compounds are limited by the toxicity and flammability of the solvents. To obtain pure extracts, it is always a longer process that requires several steps. Supercritical fluid extraction (SFE) is a cutting-edge green technology that is continuously increasing and expanding its fields of application, with benefits such as no waste produced, shorter extraction time, automation, and lower solvent consumption. The SFE of natural pigments has high potential in food, textiles, cosmetics, and pharmaceuticals; there are a number of other applications that can benefit from the SFE technique of natural pigments. The pigments that are extracted via SFE have a high potential for application and sustainability because of their biological and antimicrobial properties as well as low environmental risk. This review provides an update on the SFE technique, specifically as it pertains to the optimization of health-promoting pigments. This review focuses on antimicrobial pigments and the high efficiency of SFE in extracting pure antimicrobial pigments. In addition, the optimal conditions, biological activities, and possible applications of each category are explained.
The development of antibacterial coatings for footwear components is of great interest both from an industry and consumer point of view. In this work, the leather material was developed taking advantage of the intrinsic antibacterial activity and coloring ability of selenium nanoparticles (SeNPs). The SeNPs were synthesized and implemented into the leather surface by using ultrasonic techniques to obtain simultaneous coloring and functionalization. The formation of SeNPs in the solutions was evaluated using UV/Vis spectroscopy and the morphology of the NPs was determined by transmission electron microscopy (TEM). The treated leather material (leather/SeNPs) was characterized by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX). The effects of SeNPs on the coloration and antibacterial properties of the leather material were evaluated. The results revealed that the NPs were mostly spherical in shape, regularly distributed, and closely anchored to the leather surface. The particle size distribution of SeNPs at concentrations of 25 mM and 50 mM was in the range of 36–77 nm and 41–149 nm, respectively. It was observed that leather/SeNPs exhibited a higher depth of shade compared to untreated ones, as well as excellent fastness properties. The results showed that leather/SeNPs can significantly enhance the antibacterial activity against model of bacteria, including Gram-positive bacteria (Bacillus cereus) and Gram-negative bacteria (Pseudomonas aeruginosa, Salmonella typhi and Escherichia coli). Moreover, the resulting leather exhibited low cytotoxicity against HFB4 cell lines. This achievement should be quite appealing to the footwear industry as a way to prevent the spread of bacterial infection promoted by humidity, poor breathability and temperature which promote the expansion of the microflora of the skin.
This study aims to develop multifunctional pile cotton fabrics by implementing different compositions of lycra yarns with different densities of the cotton fabric under study. Highly dispersed silica nanoparticles (SiO2 NPs) with small sizes—in the range of 10–40 nm—were successfully prepared and were analyzed using scanning electron microscopy (SEM). The particle size distribution of nano silica was determined via dynamic laser scattering (DLS) and measurements of its zeta potential. Cotton/lycra fabrics were treated using prepared SiO2 NPs in presence of ethylenediaminetetraacetic acid (EDTA) as a crosslinking agent. Energy dispersive X-ray (EDX) analysis and scanning electron microscopy (SEM) were used to characterize the nano-treated fabrics and assure homogeneous dispersion of SiO2 NPs on the cotton/lycra composites. Additionally, the nanoparticles were screened for their in vitro antibacterial activity against human pathogens such as Gram-positive Staphylococcus aureus and Bacillus cereus and Gram-negative Escherichia coli and Pseudomonas aeruginosa strains. The functional properties of the new composite pile cotton fabrics include excellent antibacterial, highly self-cleaning, and excellent UV protection factor (UPF) properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.