Graphene nanoplatelets (GNPs), synthesized using potassium permanganate-based oxidation and exfoliation followed by reduction with hydroiodic acid (rGNP-HI), have intercalated manganese ions within the graphene sheets, and upon functionalization with iodine, show excellent potential as biomodal contrast agents for magnetic resonance imaging (MRI) and computed tomography (CT). Structural characterization of rGNP-HI nanoparticles with low- and high-resolution transmission electron microscope (TEM) showed disc-shaped nanoparticles (average diameter, 200 nm, average thickness, 3 nm). Energy dispersive X-ray spectroscopy (EDX) analysis confirmed the presence of intercalated manganese. Raman spectroscopy and X-ray diffraction (XRD) analysis of rGNP-HI confirmed the reduction of oxidized GNPs (O-GNPs), absence of molecular and physically adsorbed iodine, and the functionalization of graphene with iodine as polyiodide complexes (I3− and I5−). Manganese and iodine content were quantified as 5.1 ± 0.5 and 10.54 ± 0.87 wt% by inductively-coupled plasma optical emission spectroscopy and ion-selective electrode measurements, respectively. In vitro cytotoxicity analysis, using absorbance (LDH assay) and fluorescence (calcein AM) based assays, performed on NIH3T3 mouse fibroblasts and A498 human kidney epithelial cells, showed CD50 values of rGNP-HI between 179-301 µg/ml, depending on the cell line and the cytotoxicity assay. CT and MRI phantom imaging of rGNP-HI showed high CT (approximately 3200% greater than HI at equimolar iodine concentration) and MRI (approximately 59% greater than equimolar Mn2+ solution) contrast. These results open avenues for further in vivo safety and efficacy studies towards the development of carbon nanostructure-based multimodal MRI-CT contrast agents.
In this study, we introduce a novel nanoparticle-enhanced biophysical stimulus based on the photoacoustic (PA) effect. We demonstrate that the PA effect differentiates bone marrow-derived marrow stromal cells (MSCs) grown on poly(lactic-co-glycolic acid) (PLGA) polymer films toward osteoblasts. We further show that the osteodifferentiation of the MSCs due to PA stimulation is significantly enhanced by the presence of single-walled carbon nanotubes (SWCNTs) in the polymer. MSCs, without the osteogenic culture supplements (0.01 M bglycerophosphate, 50 mg/L ascorbic acid, 10 -8 M dexamethasone), were seeded onto plain glass slides, glass slides coated with PLGA, or glass slides coated with SWCNT-PLGA films and photoacoustically stimulated by a 527 nm Nd:YLF pulse laser, with a 200 ns pulse duration, and 10 Hz pulse frequency for 10 min a day for 15 consecutive days. The study had four control groups; three baseline controls similar to the three experimental groups but without PA stimulation, and one positive control where MSCs were grown on glass slides without PA stimulation but with osteogenic culture supplements. The osteogenic differentiation of all the groups was evaluated using quantitative assays (alkaline phosphatase, calcium, osteopontin) and qualitative staining (alizarin red). After 15 days, the PA stimulated groups showed up to a 350% increase in calcium content when compared with the non-PA stimulated positive control. Further, within the PA stimulated group, the PLGA-SWCNT group had 130% higher calcium values than the PLGA film without SWCNTs. These results were further corroborated by the analysis of osteopontin secretion, alkaline phosphatase expression, and qualitative alizarin red staining of extracellular matrix calcification. The results indicate that PA stimulation holds promise for bone tissue engineering and that the nanomaterials which enhance the PA effect should allow the development of biophysical rather than biochemical strategies to induce osteoinductive properties into tissue engineering scaffolds.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.