The effects of mold temperatures on the microstructures and mechanical properties of thixoforged Grp (graphite particles)/AZ91D composites have been investigated, followed by partial remelting and thixoforging technology. The results indicate that the best semi-solid microstructure could be obtained after being partially remelted at 600 °C and held for 60 min. Correspondingly, under a mold temperature of 300 °C, the best tensile properties were obtained by thixoforging. The UTS (ultimate tensile strength) and elongation of the thixoforged Grp/AZ91D were up to 304.1 MPa and 13.9%, respectively, which increased 11.3% and 43.1% in comparison with the thixoforged AZ91D, respectively. The variation of the tensile properties responded to the influences of mold temperatures on the amount of eutectic phase, the distribution of Grp, and the grain size of α-Mg. Meanwhile, HRTEM (High Resolution Transmission Electron Microscope) showed good bonding between Grp and AZ91D, and many edge dislocations were found in the inverse FFT (Fast Fourier Transform) image. And the result showed that the increase in tensile properties is attributed to the synergistic effect of load transfer, dislocation strengthening, and Orowan looping mechanisms from the Grp strengthening the matrix.
The effects of Grp (graphite particles) addition and holding time on the microstructure and mechanical properties of the Grp/AZ91D composite were investigated in this work. The results indicated that the distribution of Grp in the matrix was determined by the self-stabilizing mechanism and relationships between the solidifying interface and the particles. Due to the self-stabilizing mechanism, a small amount of Grp would uniformly distribute in the melt alloy, and as the amount of Grp increased, agglomeration would occur. Accordingly, the former would be engulfed by the solidifying interface and the latter would be pushed. With an increased holding time, Grp tended to agglomerate, due to the interfacial reaction that occurred, and as a result, the solidifying interface will push it. The Grp/AZ91D composite with the addition of 1.5 wt% Grp and a holding time of 15 min obtained grains 30.2 μm in size with a hardness of 89.07 HV, which was a decrease of 83.04% and increase of 35.06% compared to AZ91D, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.