Understanding the relative humidity (RH) response of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) is critical for improving the stability of organic electronic devices and developing selective sensors. In this work, combined gravimetric sensing, nanoscale surface probing, and mesoscale optoelectronic characterization are used to directly compare the RH dependence of electrical and optical conductivities and unfold connections between the rate of water adsorption and changes in functional properties of PEDOT:PSS film. We report three distinct regimes where changes in electrical conductivity, optical conductivity, and optical bandgap are correlated with the mass of adsorbed water. At low (RH < 25%) and high (RH > 60%) humidity levels, dramatic changes in electrical, optical, and structural properties occur, while changes are insignificant in mid-RH (25 < RH < 60%) conditions. We associate the three regimes with water adsorption at hydrophilic moieties at low RH, diffusion and swelling throughout the film at mid-RH, and saturation of the film by water at high RH. Optical film thickness increased by 150% as RH was increased from 9 to 80%. Low frequency (1 kHz) impedance increased by ∼100%, and film capacitance increased by ∼30% as RH increased from 9 to 80% due to an increase in the film dielectric constant. Changes in electrical and optical conductivities concomitantly decrease across the full range of RH tested.

Aqueous solubility of copper phthalocyanine-3,4′,4″,4″′-tetrasulfonic acid tetrasodium salt (CuPcTs) enables fabrication of flexible electronic devices by low cost inkjet printing. We (1) investigate water adsorption kinetics on CuPcTs for better understanding the effects of relative humidity (RH) on hydrophilic phthalocyanines, and (2) assess CuPcTs as a humidity-sensing material. Reaction models show that H2O undergoes 2-site adsorption which can be represented by a pair of sequentially-occurring pseudo-first order reactions. Using high frequency (300–700 THz) and low frequency (1–8 MHz) dielectric spectroscopy combined with gravimetric measurements and principal component analysis, we observe that significant opto-electrical changes in CuPcTs occur at RH ≈ 60%. The results suggest that rapid H2O adsorption takes place at hydrophilic sulfonyl/salt groups on domain surfaces at low RH, while slow adsorption and diffusion of H2O into CuPcTs crystallites leads to a mixed CuPcTs-H2O phase at RH > 60%, resulting in high frequency dielectric screening of the film by water and dissociation of Na+ from CuPc(SO3 −)4 ions. The CuPcTs-H2O interaction can be tracked using a combination of gravimetric, optical, and electrical sensing modes, enabling accurate ( ± 2.5%) sensing in the ~0–95% RH range with a detection limit of less than 0.1% RH.