Selection of an appropriate nickel–titanium (NiTi) rotary system is important for minimally invasive endodontic treatment, which aims to preserve as much root canal dentin as possible. This study aimed to evaluate selected mechanical properties and the root canal shaping ability of TruNatomy (TRN), a NiTi rotary system designed for minimally invasive endodontic shaping, in comparison with existing instruments: HyFlex EDM (HEDM), ProTaper Next (PTN), and WaveOne Gold (WOG). Load values measured with a cantilever bending test were ranked as TRN < HEDM < WOG < PTN (p < 0.05). A dynamic cyclic fatigue test revealed that the number of cycles to fracture was ranked as HEDM > WOG > TRN > PTN (p < 0.05). Torque and vertical force generated during instrumentation of J-shaped artificial resin canals were measured using an automated instrumentation device connected to a torque and vertical force measuring system; TRN exhibited smaller torque and vertical force values in most comparisons with the other instruments. The canal centering ratio for TRN was smaller than or comparable to that for the other instruments except for WOG at the apex level. Under the present experimental conditions, TRN showed higher flexibility and lower torque and vertical force values than the other instruments.

This study aimed to evaluate how various rotational modes influence the torque/force production and shaping ability of ProTaper Universal (PTU; non-heat-treated) and ProTaper Gold (PTG; heat-treated) nickel–titanium instruments. J-shaped resin canals were instrumented with PTU or PTG using an automated instrumentation device operated with reciprocating rotation [150° clockwise and 30° counterclockwise (R150/30) or 240° clockwise and 120° counterclockwise (R240/120)], optimum torque reverse motion (OTR), or continuous rotation (CR) (n = 10 each). Maximum force and torque were recorded, and canal centering ratios were calculated. Statistical analysis was performed with two-way ANOVA and a Bonferroni test (α = 0.05). The results were considered with reference to previous studies on the microstructure of the instruments. The upward force generated by R240/120 and OTR was smaller than that generated by R150/30 and CR in PTG (p < 0.05). The clockwise torque produced by OTR was lower than that produced by R150/30 in PTU and R240/120 and CR in PTG (p < 0.05). R240/120 and OTR induced less canal deviation compared to CR in PTU at 0 mm from the apex (p < 0.05). In conclusion, R240/120 and OTR reduced the screw-in force in PTG and improved the canal centering ability in PTU, which may be associated with the heat treatment-induced microstructural difference of the two instruments.

Background The aim of this study was to evaluate the phase composition, phase transformation temperatures, bending property, and cyclic fatigue resistance of differently heat-treated nickel-titanium (NiTi) rotary instruments with the same tip diameter and taper at room (RT; 25 ± 1 °C) and body (BT; 37 ± 1 °C) temperatures. Methods Five heat-treated NiTi rotary instruments, HyFlex EDM (EDM), HyFlex CM (CM), Vortex Blue (VB), RE file CT (RE) and JIZAI, and a non-heat-treated NiTi rotary instrument (Mtwo) with a size 40, 0.04 taper were investigated. Temperature-dependent phase transformation was examined with differential scanning calorimetry (DSC). The bending loads of the instruments at RT and BT were evaluated using a cantilever-bending test. Cyclic fatigue resistance at RT and BT was measured using a dynamic test, during which the instruments were rotated in combination with a 2-mm back-and-forth motion in an artificial curved canal, and the number of cycles to failure (NCF) was determined. The results were analyzed using two-way repeated measures analysis of variance, a simple main effect test, and the Bonferroni test (α = 0.05). Results DSC results indicated that EDM and Mtwo were primarily composed of martensite/R-phase and austenite, respectively, while the other heat-treated instruments were composed of a mix of martensite/R-phase and austenite at the tested temperatures. Regardless of the temperature setting, the bending loads of heat-treated instruments were significantly lower than those of Mtwo (p < 0.05). EDM showed the lowest bending loads and highest NCF at both temperatures (p < 0.05). CM, VB, and JIZAI showed significantly higher bending loads at BT than at RT (p < 0.05). The NCF of all the heat-treated instruments, except VB, was lower at BT than at RT (p < 0.05). At BT, the NCF of CM, RE, and JIZAI were not significantly higher than that of Mtwo (p > 0.05). Conclusions Heat-treated NiTi instruments exhibited lower bending loads and higher NCF values than Mtwo. However, this tendency was less pronounced at BT than at RT, particularly in instruments composed of a mix of martensite/R-phase and austenite.