Electrochemical corrosion testing was used to evaluate the corrosion resistance of four different nickel-based alloys, namely UNS N06230, UNS N06025, UNS N06617, and UNS N06625, in a molten nitrate salt that is used as a heat transfer media and thermal energy storage material in solar-thermal power plants. The tests were conducted at 500 °C to simulate near-maximum service temperature in the 3:2 by weight sodium nitrate: potassium nitrate mixture. All tested samples had corrosion current densities on the order of 10−4 A cm−2 with corrosion potentials varying from −227 mV to −66.2 mV vs Pt. The tested samples exhibited low corrosion current density in the range of 0.225 mA cm−2 to 0.431 mA cm−2. The morphology of the samples surfaces was studied using scanning electron microscopy which showed the formation of a surface film on all samples. Cross-sectional analysis was performed using focused ion beam scanning electron microscopy. The surface chemistry was ascertained using energy dispersive spectroscopy, X-ray diffraction, Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). Raman spectra paired with XPS suggested the formation of various nickel-chromium-iron spinels on UNS N06625. These results show that UNS N06625 has the potential to be a material for use in solar-thermal plants.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.