No abstract

The enthalpies of formation for the compounds (RE3+)PO4, (where RE = Sc, Y, La–Nd, Sm–Lu) were determined by oxide-melt solution calorimetry. Calorimetric measurements were performed in a Calvet-type twin microcalorimeter in sodium molybdate (3Na2O · 4MoO3) and lead borate (2PbO · 2B2O3) solvents at 975 K. The experiments were carried out using both powdered single crystals grown by a flux technique and powders synthesized by precipitation. Formation enthalpies were derived from the drop-solution enthalpies for (RE)PO4, RE oxides, and P2O5. Enthalpies of formation for the (RE)PO4 compounds with respect to the oxides at 298 K become more negative with increasing RE3+ ionic radius; i.e., in going from ScPO4 (−209.8 ± 1.0 kJ/mol), to LuPO4 (−263.9 ± 1.9 kJ/mol), to LaPO4 (−321.4 ± 1.6 kJ/mol). From structural considerations, a similar trend is expected for the isostructural RE vanadates and arsenates, as well as for the tetravalent actinide orthosilicates.

Minerals containing peroxide are limited to studtite, (UO2)O2(H2O)4, and metastudtite, (UO2)O2(H2O)2. High-temperature oxide-melt solution calorimetry and solubility measurements for studtite (standard enthalpy of formation at 298 kelvin is -2344.7 +/- 4.0 kilojoules per mole from the elements) establishes that these phases are stable in peroxide-bearing environments, even at low H2O2 concentrations. Natural radioactivity in a uranium deposit, or the radioactivity of nuclear waste, can create sufficient H2O2 by alpha radiolysis of water for studtite formation. Studtite and metastudtite may be important alteration phases of nuclear waste in a geological repository and of spent fuel under any long-term storage, possibly at the expense of the commonly expected uranyl oxide hydrates and uranyl silicates.

The lanthanide stannates, Ln2Sn2O7, Ln=La-Lu and Y, have the isometric pyrochlore structure, A2B2O7, and their structural properties have been refined by Rietveld analysis of powder neutron and synchrotron X-ray diffraction data. In this study, the enthalpies of formation of selected stannate pyrochlores, Ln=La, Nd, Sm, Eu, Dy, and Yb, were measured by high-temperature oxide melt solution calorimetry. Their radiation response was determined by 1 MeV Kr2+ ion irradiation combined with in situ TEM observation over the temperature range of 25 to 1000 K. The enthalpy of formation from binary oxides of stannate pyrochlores became more endothermic (from -145 to -40 kJ/mol) as the size of the lanthanide in the A-site decreases. A more exothermic trend of the enthalpy of formation was observed in stannate pyrochlores with larger lanthanide ions, particularly La, possibly as a result of increased covalency in the Sn-O bond. In contrast to lanthanide titanate pyrochlores, Ln2Ti2O7, that are generally susceptible to radiation-induced amorphization and zirconate pyrochlores, Ln2Zr2O7, that are generally resistant to radiation-induced amorphization, the lanthanide stannate pyrochlores show a much greater variation in their response to ion irradiation. La, Nd, and Gd stannates experience the radiation-induced transformation to the aperiodic state, and the critical amorphization temperatures are approximately 960, 700, and 350 K, respectively. Y and Er stannate pyrochlores cannot be amorphized by ion beam irradiation, even at 25 K, and instead disorder to a defect fluorite structure. Comparison of the calorimetric and ion irradiation data for titanate, zirconate, and stannate pyrochlores reveals a strong correlation among subtle changes in crystal structure with changing composition, the energetics of the disordering process, and the temperature above which the material can no longer be amorphized. In summary, as the structure approaches the ideal, ordered pyrochlore structure, radiation-induced amorphization is more easily attained. This is consistent with an increasingly exothermic trend in the enthalpies of formation of pyrochlores from the oxides, that is, the greater the thermochemical stability of the pyrochlore structure, the more likely it will be amorphized upon radiation damage rather than recover to a disordered fluorite structure.