Hot Isostatic Pressing (HIP) can be used to increase the fatigue limit of additively manufactured metals. However, with no further surface treatment, its contribution might be restricted by a rough surface. We thus tested Ti6Al4V alloy prepared by selective laser melting in the as-built surface condition to evaluate the utility of HIP. The influence of HIP on microstructure, static mechanical properties and fatigue was evaluated in comparison with untreated and conventionally heat treated state.

No abstract

No abstract

No abstract

This paper explores the influence of sample thickness and build orientation on the microstructure and mechanical properties of electron beam melting (EBM) additive manufactured Ti-6Al-4V titanium alloy and compared to previously published work on SLM-processed material. In particular, the various mechanical properties (tensile yield strength, ultimate tensile strength) were investigated with attempts to correlate with various microstructural features, including lamellae thickness, porosity and the size of prior-beta grains. However, it is shown that the surface exerts a dominant effect on mechanical properties with as-deposited surfaces. These observations provide the possibility for the further improvement of processing/property relations with as-deposited surfaces.

This work deals with the application of the Conform SPD (Severe Plastic Deformation) continuous extrusion process for ultrafine to nanostructured pure titanium production. The process has been derived from the Equal Channel Angular Pressing (ECAP) technique but, unlike ECAP, it offers continuous production of high-strength wire. This study describes the Conform SPD process combined with subsequent cold working (rotary swaging technique), its potential for commercial application, and the properties of high-strength wires of pure titanium. High-strength wire of titanium Grade 4 is the product. Titanium Grade 4 reaches ultimate strengths up to 1320 MPa. This value is more than twice the ultimate strength of the unprocessed material. The typical grain size upon processing ranges from 200 to 500 nm. Process development supported by FEM analysis together with detailed microstructure characterization accompanied by mechanical properties investigation is presented.

No abstract

No abstract