Copper(II) selenide, CuSe was prepared from Cu and Se powders in a stoichiometric ratio by a rapid, and convenient one-step mechanochemical synthesis, after 5 and 10 min of milling in a planetary, and an industrial vibratory, mill. The kinetics of the synthesis, and the structural, morphological, optical, and electrical properties of CuSe products prepared in the two types of mill were studied. Their crystal structure, physical properties, and morphology were characterized by X-ray diffraction, specific surface area measurements, particle size distribution, scanning, and transmission electron microscopy. The products crystallized in a hexagonal crystal structure. However, a small amount of orthorhombic phase was also identified. The scanning electron microscopy revealed that both products consist of agglomerated particles of irregular shape, forming clusters with a size ~50 mm. Transmission electron microscopy proved the nanocrystalline character of the CuSe particles. The optical properties were studied using UV–Vis and photoluminescence spectroscopy. The determined band gap energies of 1.6 and 1.8 eV for the planetary- and vibratory-milled product, respectively, were blue-shifted relative to the bulk CuSe. CuSe prepared in the vibratory mill had lower resistivity and higher conductivity, which corresponds to its larger crystallite size in comparison with CuSe prepared in the planetary mill.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.