Chitosan is a marine-derived product that has been widely used in clinical applications, especially in skin reconstruction. The mammalian scaffolds derived from bovine and porcine material have many limitations, for example, prion transmission and religious concerns. Therefore, we created a chitosan skin regenerating template (SRT) and investigated the behavior of fibroblast cell-scaffold constructs. Primary human dermal fibroblasts (HDF) were isolated and then characterized using vimentin and versican. HDF were seeded into chitosan SRT at a density of 3×106 cells/cm2 for fourteen days. Histological analysis and live cells imaging revealed that the cell-chitosan constructs within interconnected porous chitosan showed significant interaction between the cells as well as between the cells and the chitosan. Scanning electron microscopy (SEM) analysis revealed cells spreading and covering the pores. As the pore sizes of the chitosan SRT range between 40–140 μm, an average porosity is about 93 ± 12.57% and water uptake ratio of chitosan SRT is 536.02 ± 14.29%, it is a supportive template for fibroblast attachment and has potential in applications as a dermal substitute.
The aim of this paper was to investigate the effects of cross-linked reaction on physicochemical properties of chitosan film by using genipin as cross-linker agent. Series of chitosan film samples with different amount concentration of genipin loaded (0-3 wt %) were prepared and characterized. The physicochemical properties of films were evaluated by Fourier Transform Infra-red (FTIR), UV-vis spectroscopy, Oxygen Transmission Rate (OTR), Scanning Electron Microscopy (SEM), water vapour and tensile test. The cross-linking reaction had affected on colour changing of chitosan film samples from light yellow to dark blue in line with the increasing of genipin concentration. Thus, UV-vis spectroscopy on the cross-linked samples showed the absorbance value at 600 nm wavelength due to genipin content. FTIR observation on cross-linked film samples showed no characteristic of –OCH3 peak from genipin at 1444 cm-1 which resulted by new covalent bonding occurred between chitosan and genipin. Cross-linking also had increased the oxygen barrier and reduced the water vapor rate through the film. Chitosan film sample with addition of 1 wt% genipin achieved the highest tensile stress average at 49.46 MPa compared to other samples while percent of elongation at break reduced with the increasing of genipin concentration loaded
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.