The paper presents the results of research concerning the influence of a metallic micromaterial on the thermal conductivity λ, specific heat Cp, and thermal diffusivity a of modified geopolymers. Iron oxide in the form of powder with an average granulation of 10 μm was used as the geopolymer-modifying material. The research concerned geopolymer composite samples with metakaolin (activated with potassium silicate) and the addition of iron in amounts ranging from 0.5% to 2.5% in relation to the weight of the metakaolin. Additionally, the samples were modified with sand and fireclay in two different amounts—1:1 and 1:1.2 in relation to the metakaolin. The addition of fireclay caused a decrease in the thermal conductivity of the composites by 30% when compared to the samples with the addition of sand. The lowest value of the thermal conductivity coefficient λ was obtained for the geopolymer with metakaolin and fireclay. When the ratio of these components in the composite was 1:1, the value of thermal conductivity was equal to 0.6413 W/(m·K), while in the case of their ratio being 1:1.2, it was equal to 0.6456 W/(m·K). In the samples containing fireclay, no significant influence of the added iron on the values of thermal conductivity was noticed. In the case of the geopolymer with sand, the effect was noticeable, and it was most visible in the samples containing metakaolin and sand in the ratio of 1:1.2. It was noticed that with an increase in the addition of Fe, the thermal conductivity of the composite increased.
The paper presents the results of research concerning the influence of micromaterials on the heat conductivity coefficient λ, specifically heat Cp and thermal diffusivity a of modified gypsum and geopolymer. Microspheres, hydroxyethyl methylcellulose (HEMC) polymer, and aerogel were used as the gypsum’s modifying materials. The study also investigated an alkali potassium-activated methakaolin-based geopolymer with the addition of aluminium dust. During the measurements of thermal parameters, the nonstationary method was chosen, and an Isomet device—which recorded the required physical quantities—was used. When compared to the reference sample, a decrease in the thermal conductivity and diffusivity of the hardened gypsum— and a simultaneous increase in specific heat—was observed with the addition of micromaterials. The geopolymer sample was characterized by the lowest value of thermal conductivity, equal to 0.1141 W/(m·K). It was over 62% lower than the reference sample containing only gypsum. The experimental values of the thermal conductivity of the gypsum samples with the addition of HEMC, aerogel and microspheres were, respectively, over 23%, 6%, and 8% lower than those of the unmodified gypsum samples. The lowest values of thermal conductivity were observed in the case of the gypsum samples modified with polymer; this resulted from the fact that the polymer caused the greatest change in the structure of the gypsum’s composite, which were expressed by the lowest density and highest porosity.
The paper presents an assessment of the impact of using additives on the strength of a binding material, i.e., building gypsum, and also the phase transformation that takes place in it. Microspheres, aerogel and polymer (HEMC) additives were added to a building gypsum slurry with a water to gypsum ratio of 0.75. In order to investigate their influence on bending strength, compressive strength, and the effect of high temperatures, differential scanning calorimetry (DSC), as well as tests of the multicomponent binder, were carried out in accordance with the applicable PN-EN 13279-2:2005 standard. The obtained test results allowed to determine that the used additives influenced the strength parameters of the obtained composites. It was shown that the applied additives decreased the compressive and bending strength of the modified gypsum. Despite these properties, the obtained gypsum materials are environmentally friendly because they reuse wastes, such as microspheres. Out of all the applied additives, the use of microspheres in an amount of 10% caused a decrease in the bending strength by only 10%, and an increase in the compressive strength by 4%.
This paper reports the results of an experimental investigation on the mechanical properties of geopolymer foams incorporating filler from the coke dust waste (CDW). In this work, CDW was used to replace a part of geopolymer paste at 5%, 10%, 20%, and 30% by geopolymer binder mass. The physico-mechanical properties and thermal resistance against high temperatures of CDW/geopolymer foams are presented. The primary results obtained show that the use of CDW in the production of geopolymer foam composites made it possible for them to achieve relatively good mechanical properties. However, the incorporation of the CDW into the geopolymer had a slightly negative effect on thermal conductivity, but significantly improved the mechanical strength of the final product. Moreover, this waste also helped the composite foam to achieve a structure with more uniform open pores distribution, compared to the pure foam. After exposure to elevated temperatures, the residual strength of the composite foams maintained well compared to the pure foams.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.