In this work, a manganese selenide/graphene oxide (MnSe/GO)-based composite was prepared for wet-chemical assisted method against organic dye; herein, methylene blue (MB) dye removal from the water was employed as a metal selenide-based photocatalyst. The synthesized MnSe/GO composite was systematically characterized by X-ray diffraction (XRD), Fourier transform electron microscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and UV-visible diffuse reflectance spectroscopy (UV-vis. DRS). The structural characteristic revealed the adequate synthesis of the sample with good crystallinity and purity of the obtained products. The morphological analysis indicates the formation of MnSe nanoflakes composed of tiny particles on their surface. At the same time, the GO nanosheets with high aggregation were formed, which may be due to the van der Waals forces. The bond interaction and compositional analysis studies confirmed and supported the structural findings with high purity. The optical analysis showed the bandgap energies of MnSe and their composites MnSe (1.7 eV), 7% GO-MnSe (2.42 eV), 14% GO-MnSe (2.6 eV), 21% GO-MnSe (3.02 eV), and 28% GO-MnSe (3.24 eV) respectively, which increase the bandgap energy after GO and MnSe recombination. Among different contents, the optimized 21% GO-MnSe composite displayed enhanced photocatalytic properties. For instance, a short time of 90 min was taken compared with other concentrations due to the narrow bandgap of MnSe and the highly conductive charge carrier’s support, making the process to remove MB from water faster. These results show that the selenide-based photocatalyst can be an attractive candidate for future advanced photocatalysis applications.

No abstract

No abstract

No abstract

No abstract

No abstract

No abstract

The main objective of this work is to recycle unwanted industrial waste in order to produce innovative nanocomposites with improved mechanical, tribological, and thermal properties for use in various industrial purposes. In this context, powder metallurgy (PM) technique was used to fabricate iron (Fe)/copper (Cu)/niobium carbide (NbC)/granite nanocomposites having outstanding mechanical, wear and thermal properties. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) examinations were used to investigate the particle size, crystal size, and phase composition of the milled samples. Additionally, it was investigated how different volume percentages of the NbC and granite affected the sintered specimens in terms of density, microstructure, mechanical and wear properties, and coefficient of thermal expansion (CTE). According to the findings, the milled powders included particles that were around 55 nm in size and clearly contained agglomerates. The results showed that the addition of 4 vol.% NbC and 8 vol.% granite nanoparticles caused a reduction in the Fe–Cu alloy matrix particle sizes up to 47.8 nm and served as a barrier to the migration of dislocations. In addition, the successive increase in the hybrid concentrations led to a significant decrease in the crystal size of the samples prepared as follows: 29.73, 27.58, 22.69, 19.95 and 15.8 nm. Furthermore, compared with the base Fe–Cu alloy, the nanocomposite having 12 vol.% of hybrid reinforcement demonstrated a significant improvement in the microhardness, ultimate strength, Young’s modulus, longitudinal modulus, shear modulus, bulk modulus, CTE and wear rate by 94.3, 96.4, 61.1, 78.2, 57.1, 73.6, 25.6 and 61.9%, respectively. This indicates that both NbC and granite can actually act as excellent reinforcements in the Fe alloy.