High strength concrete is usually cast with low water-to-binder ratio (w/b) in order to produce a compact microstructure with high strength and durability. Autoclave curing can accelerate cement hydration and pozzolanic reactions and further modify microstructure of cement pastes (such as decreasing the Ca/Si ratio and forming crystallized calcium silicate hydrate). The present paper evaluates the effect of w/b ratio, in the range 0.20 -0.40, on compressive strength, porosity and microstructure of a high strength concrete. Some samples were subjected to autoclave curing in order to evaluate the effect of this process on the parameters evaluated. The microstructure was evaluated using X-ray diffraction and scanning electron microscopy. The results show the porosity decreased when w/b ratio decreased from 0.40 to 0.30 and thereafter the total porosity remained virtually constant while the water permeable porosity increased. An inverse relationship is observed between the porosity and the compressive strength. Autoclave curing affects significantly the phases developed in hardened concrete. It accelerates hydration and pozzolanic reactions, affects the interfacial transition zone and triggers the formation of crystalline C-S-H. These changes reflect in improved compressive strength at a low w/b but its effect is negligible at moderate w/b ratios.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.