A range of talc-like phyllosilicates were prepared via a hydrothermal synthesis performed at five different temperatures from 160 to 350 C. The organization of the lattice and the degree of crystallinity of the new materials were evaluated by different techniques such as XRD, FTIR, solid-state 29 Si NMR, TEM, FEG-SEM and TG-DTA. When synthesized at low temperature the material presents high degree of hydration, low crystallinity and flawed structure. This was attributed to stevensite-talc interstratified product present in the samples. The stevensite/talc ratio and the hydration decrease in the talc-like phyllosilicate samples when the hydrothermal synthesis temperature increases and so the crystallinity becomes higher. A thermal treatment at 500 C allowed a significant flaw reduction in talclike phyllosilicate structure; the synthesized sample at 350 C and heat treated presents a structure close to that of talc. The different talc-like phyllosilicates were grafted covalently by two organoalkoxysilane reagents, N-(3-triethoxysilylpropyl)-4,5-dihydroimidazole (IM2H) and 2-hydroxy-4-(3triethoxysilylpropoxy)-diphenylketone (HTDK). The grafted amounts of the hybrids, determined by elemental analysis and confirmed by thermogravimetric data, are dependent on the hydrothermal synthesis temperature and organoalkoxysilanes; they become smaller when the synthesis temperature increases and when HTDK is used. FTIR and solid-state 13 C CP MAS NMR were applied to characterize the grafted organic groups. So, in this work it is shown that by choosing the hydrothermal synthesis temperature or by performing an additional annealing it is possible to adjust the amount of defects in the structure of talc-like phyllosilicates which seems to be strongly correlated to the grafting performance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.