We investigated the effect of the substrate temperature on the electrical and the optical properties of ZnO/4H-SiC structures. The n-type ZnO layer was grown on p-type 4H-SiC substrate by pulsed laser deposition to form p-n hetero-junction diode structure. The n-type ZnO thin films were deposited by pulsed laser deposition at different temperatures of 200, 400, and 600 °C, respectively. It was shown from transmission line method (TLM) and auger electron spectroscopy (AES) data that the sheet resistance of ZnO on SiC was increases from ~760 Ω/square to ~4000 Ω/square as the deposition temperature increases and the oxygen outdiffusion decreases. The I-V characteristics with and without illumination has also been studied.
The characteristics of Ga-doped zinc oxide (GaZnO) thin films deposited at different substrate temperatures (TS~250 to 550oC) on 4H-SiC have been investigated. Structural and electrical properties of GaZnO thin film on n-type 4H-SiC (100)were investigated by using x-ray diffraction, atomic force microscopy (AFM), Hall effect measurement, and Auger electron spectroscopy (AES). Hall mobility is found to increase as the substrate temperature increase from 250 to 550 oC, whereas the lowest resistivity (~3.3 x 10-4 Ωcm) and highest carrier concentration (~1.33x1021cm-3) values are observed for the GaZnO films deposited at 400 oC. It has been found that the c-axis oriented crystalline quality as well as the relative amount of activated Ga3+ Introduction ions may affect the electrical properties of GaZnO films on SiC.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.