The effect of different fabricating processes (spray forming and conventional casting) and homogenization treatment on the microstructure of an 7055 alloy was investigated by optical microscopy (OM), scanning electron microscopy (SEM), electron probe X-ray micro-analyzer (EPMA), and transmission electron microscopy (TEM). It was found that the grain size of the as-deposited (spray formed) 7055 alloy had half the size as that of the as-cast 7055 alloy and there was no Al 2 CuMg phase that embedded in the coarse Mg(Zn, Cu, Al) 2 phase distributed along the grain boundaries in the as-deposited 7055 alloy. No segregation of zirconium was observed in the as-deposited 7055 alloy. After homogenization heating at 350°C/5 hours + 470°C /24 hours, Al 3 Zr dispersoids were inhomogeneously distributed within grains in the traditionally cast 7055 alloy, while more homogeneously distributed within grains in the spray-formed 7055 alloy. Compared with the traditional cast 7055 alloy, the uniform distribution of Al 3 Zr dispersoids in the spray-formed 7055 alloy retards recrystallization more effectively. This investigation highlights the advantage of spray forming technology on improving microstructure of a 7055 alloy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.