Grafting hyperbranched polyglycerols onto a carbon fiber surface is done in an attempt to improve the interfacial and impact properties between carbon fiber and epoxy resin. Scanning electron microscopy (SEM), thermal gravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS) and dynamic contact angle analysis were performed to characterize the carbon fibers. The TGA result shows that the mass fraction of the hyperbranched polyglycerols grafted onto the carbon fibers surface was 9.03%. The SEM results indicate that the hyperbranched polyglycerols have been grafted onto the carbon surface and that the surface roughness of the carbon fiber significantly increased. The XPS result indicates that oxygen-containing functional groups obviously increased after modification. Dynamic contact angle analysis indicates that the surface energy of modified carbon fibers increased significantly compared with the untreated ones. Results of the mechanical property tests show that interfacial shear strength increased from 59.86 to 80.16 MPa, interlaminar shear strength increased from 57.57 to 73.49 MPa and impact strength simultaneously increased from 2.52 to 3.52 J.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.