A 3 wt% La-promoted Ni/Al2O3 catalyst was prepared via wet co-impregnation technique and physicochemically-characterized. Lanthanum was responsible for better metal dispersion; hence higher BET specific surface area (96.0 m2 g−1) as compared to the unpromoted Ni/Al2O3 catalyst (85.0 m2 g−1). In addition, the La-promoted catalyst possessed finer crystallite size (9.1 nm) whilst the unpromoted catalyst measured 12.8 nm. Subsequently, glycerol dry reforming was performed at atmospheric pressure and temperatures ranging from 923 to 1123 K employing CO2-to-glycerol ratio from zero to five. Significantly, the reaction results have yielded syngas as main gaseous products with H2:CO ratios always below than 2.0 with concomitant maximum 96% glycerol conversion obtained at the CO2-toglycerol ratio of 1.67. In addition, the glycerol consumption rate can be adequately captured using power law modelling with the order of reactions equal 0.72 and 0.14 with respect to glycerol and CO2 whilst the activation energy was 35.0 kJ mol−1. A 72 h longevity run moreover revealed that the catalyst gave a stable catalytic performance.
The increase in biodiesel production inevitably yield plethora of glycerol. Therefore, glycerol has been touted as the most promising source for bio-syngas (mixture of H2 and CO) production. Significantly, coking on nickel-based catalysts has been identified as a major deactivation factor in reforming technology. Indeed, coke-resistant catalyst development is essential to enhance syngas production. The current work develops cement clinker (comprised of 62.0% calcium oxide)-supported nickel catalyst (with metal loadings of 5, 10, 15 and 20 wt%) for glycerol dry reforming (CO2). Physicochemical characterization of the catalysts was performed using XRD, XRF, BET, TGA and FESEM-EDS techniques. Subsequently, reaction studies were conducted in a 7-mm ID fixed-bed stainless steel reactor at 1023 K with various CO2 partial pressures at constant weight-hourly space velocity (WHSV) of 7.2×104 ml gcat -1 h -1 . Gas compositions were determined using Agilent 3000 micro-gas chromatography (GC) and Lancom III gas analyzer. Results obtained showed an increment of BET surface area up to 32-fold with Ni loading which was corroborated by FESEM images. Syngas (H2 and CO) ratios of less than 2 were being produced at 1023 K. A closer scrutiny to the transient profile revealed that the presence of CO2 higher or lower than CGR 1:1 promotes the Boudouard reaction.
Glycerol (a bio-waste generated from biodiesel production) has been touted as a promising bio-syngas precursor via reforming route. Previous studies have indicated that carbon deposition is the major performance-limiting factor for nickel (Ni) catalyst during glycerol steam reforming. In the current paper, dry (CO2)-reforming of glycerol, a new reforming route was carried out over alumina (Al2O3)-supported nonpromoted and lanthanum-promoted Ni catalysts. Both sets of catalysts were synthesized via wet coimpregnation procedure. The physicochemical characterization of the catalyst showed that the promoted catalyst possessed smaller metal crystallite size, hence higher metal dispersion compared to the virgin Ni/Al2O3 catalyst. This was also corroborated by the surface images captured by the FESEM analysis. In addition, BET surface area measurement gave 92.05m²/g for non-promoted Ni catalyst whilst promoted catalysts showed an average of 1 to 6% improvement depending on the La loading. Reaction studies at 873 K showed that glycerol dry reforming successfully produced H2 with glycerol conversion and H2 yield that peaked at 9.7% and 25% respectively over 2wt% La content. The optimum catalytic performance by 2%La-Ni/Al2O3 can be attributed to the larger BET surface area and smaller crystallite size that ensured accessibility of active catalytic area.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.