The influence of direct incorporation of thermally efficient phase-change materials (PCMs) on the hydration and mineralogical properties of cement mortar was investigated. To assess the viability of bulk addition of PCMs to a cementitious system, tests of the early age, hydration, mechanical, durability and mineralogical properties were carried out. Organic PCMs showed an increase in setting time, while inorganic materials exhibited fast setting characteristics. Surface temperature was also found to be lower for cement paste with incremental dosages of PCM. However, chemical shrinkage was found to be reduced in the presence of PCM except for the inorganic type. It was observed from the results that PCMs negatively influenced the rate of strength development of a cementitious mortar. The slow rate of strength development was found to be attributed to interrupted hydration, which was confirmed through mineralogical studies. Further, from the thermo-gravimetric analysis, it was observed that the presence of PCMs in a cementitious system increased calcium hydroxide content and reduced the content of water related to hydration products.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.