A series of dodecyl-based monofunctional trithiocarbonate chain transfer agents (CTAs) were successfully synthesized, toward the reversible addition-fragmentations chain transfer (RAFT) polymerization of styrene. The CTAs were used as initiators for RAFT polymerization, in the absence of the conventional free radical initiator, at higher temperature. Polystyrene (PS) of narrow polydispersity index (PDI) is synthesized. Subsequently, poly(styrene-b-benzyl methacrylate) diblock and poly(styrene-b-benzyl methacrylate-b-2-vinyl pyridine) triblock copolymers were synthesized from the PS macro-RAFT agent by simply heating with the second and third monomer, respectively. These experiments suggest that it should be possible to control the RAFT polymerization initiated by a CTA through the adjustment of the temperature of polymerization in such manner that initiation is tailored to proceed at faster rate (at higher tem-perature) in comparison to propagation (lower temperature). For the specific CTAs studied in this work, the polymerization rate of styrene was high in the case of the reinitiating cyano (CN)-substituted group (R group) compared to the other groups studied.The results further show that 4-cyano pentanoic acid group is superior to the other R groups used for the RAFT polymerization of styrene, especially based on the polydispersity at a given conversion as well as the variation in the expected and experimental number-average-molecular weights.

Controlled radical polymerization of cyclohexyl methacrylate (CHMA), at ambient temperature, using various chain transfer agents (CTAs) is successfully demonstrated via single electron transfer‐radical addition fragmentation chain transfer (SET‐RAFT). Well‐controlled polymerization with narrow molecular weight distribution (Mw/Mn) < 1.25 was achieved. The polymerization rate followed first‐order kinetics with respect to monomer conversion, and the molecular weight of the polymer increased linearly up to high conversion. A novel, fluorescein‐based initiator, a novel fluorescent CTA and two other CTAs comprising of butane thiol trithiocarbonate with cyano (CTA 1) and carboxylic acid (CTA 3) as the end group were synthesized and characterized. The polymerization is observed to be uncontrolled under SET and less controlled under atom transfer radical polymerization (ATRP) condition. CTA 2 and 3 produces better control in propagation compared with CTA 1, which may be attributed to the presence of R group that undergoes ready fragmentation to radicals, at ambient temperature. The poly(cyclohexyl methacrylate) [P(CHMA)] prepared through ATRP have higher fluorescence intensity compared with those from SET‐RAFT, which may be attributed to the quenching of fluorescence by the trithiocarbonate and the long hydrocarbon chain. It is observed that block copolymers P(CHMA‐b‐t‐BMA) produced from P(CHMA) macroinitiators synthesized via SET‐RAFT result in lower polydispersity index in comparison with those synthesized via ATRP. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010

The polymerization of MMA, at ambient temperature, mediated by dansyl chloride is investigated using controlled radical polymerization methods. The solution ATRP results in reasonably controlled polymerization with PDI < 1.3. The SET‐LRP polymerization is less controlled while SET‐RAFT polymerization is controlled producing poly(methyl methacrylate) (PMMA) with the PDI < 1.3. In all the cases, the polymerization rate followed first order kinetics with respect to monomer conversion and the molecular weight of the polymer increased linearly with conversion. The R group in the CTAs do not appear to play a key role in controlling the propagation rate. SET‐RAFT method appears to be a simpler tool to produce methacrylate polymers, under ambient conditions, in comparison with ATRP and SET‐LRP. Fluorescent diblock copolymers, P(MMA‐b‐PhMA), were synthesized. These were highly fluorescent with two distinguishable emission signatures from the dansyl group and the phenanthren‐1‐yl methacrylate block. The fluorescence emission spectra reveal interesting features such as large red shift when compared to the small molecule. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012