In this work, we have carried out ivestigations on photo-electrochemical energy conversion and storage on WO 3 /TiO 2 hybrid materials. The band gap excitation of the hybrid WO 3 /TiO 2 having an amorphous WO 3 phase led to an effective photo-charging to form a tungsten bronze structure by the intercalation of protons while a reversible discharging through de-intercalation could also be observed.The photo-electrochemical conversion and storage of solar (photo) energy using semiconductors have attracted considerable interest over the last decades. Tungsten trioxide (WO 3 ) is especially interesting as a photo-anode and electro-or photo-chromic material [1][2][3][4][5][6]. On the other hand, the bicomponent WO 3 /TiO 2 has been found to exhibit higher photocatalytic reactivity for the decomposition of organic compounds than either TiO 2 or WO 3 itself [7]. Moreover, the WO 3 /TiO 2 system, with its energy storage ability, could also be applied for anticorrosion or bactericidal effects [8][9][10]. The photoinduced charge separation on WO 3 /TiO 2 to produce a hole and an electron initiates the oxidation and slow reduction of the substrates even under dark conditions, respectively. Our aim is to design such photo-functional devices as photo-chargeable batteries using a hybrid WO 3 /TiO 2 that can operate as an effective UV-light driven photo-anode for charge separation as well as charge accumulation. Here, we report on the effects of the crystallinity of WO 3 , i.e., polycrystalline or amorphous, on its photo-charging and discharging abilities using hybrid WO 3 /TiO 2 materials. ExperimentalA polycrystalline WO 3 (referred to as c-WO 3 ) and an amorphous WO 3 (a-WO 3 ) were prepared by the thermal decomposition of ammonium tungstate at 873 K for 6 h and tungstic acid (H 2 WO 4 ) at 573 K for 1 h, respectively. An a-WO 3 /TiO 2 and c-WO 3 /TiO 2 with 20 wt% WO 3 were prepared by the impregnation of ammonium tungstate into TiO 2 (anatase structure, Kanto Chemicals), and by a physical mixing of c-WO 3 with TiO 2 , respectively. Each sample was spread over a conductive indium tin oxide glass (ITO, 10 W) with triethyleneglycol as the binder, and was then calcinated in air at 773 K for 15 min. The powder X-ray diffraction (XRD) patterns of all the samples were obtained with a RIGAKU RINT2000 using Cu K a radiation (k=1.5417 Å ).The charge-discharge characteristics of these materials were measured by a potentiostat (HA-501, HOKUTO DENKO) used as a potentiometer. A black light (UV-light: 365 nm, 0.50 mW/cm 2 ) was used as the light source for the photo-charging. In the charge-discharge cycle tests, all of the electrodes were discharged at a constant current density of 10 lA/cm 2 between the photo-electrode (working electrode) and Pt wire (counter electrode). The electrolyte was adjusted to 0.5 M (COOH) 2 and 0.1 M LiClO 4 in CH 3 OH solution. The electrolyte was bubbled with N 2 gas for 30 min under vigorous stirring. Results and discussionThe characteristics of the charge-discharge properties for the photo-electrodes of TiO...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.